Connection structure and method for manufacturing connection structure

ABSTRACT

A method for manufacturing connection structure, the method includes arranging conductive particles and a first composite on a first electrode located on a first surface of a first member, arranging a second composite on the first electrode and a region other than the first electrode of the first surface, arranging the first surface and a second surface of a second member where a second electrode is located, so that the first electrode and the second electrode are opposed to each other, pressing the first member and the second member, and curing the first composite and the second composite.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is based upon and claims the benefit of priority fromthe prior Japanese Patent Application No. 2018-015667, filed on Jan. 31,2018, the entire contents of which are incorporated herein by reference.

FIELD

An embodiment of the present invention relates to a connection structurehaving a connection configuration of electrodes made of conductivecomposite and a method for manufacturing the connection structure.

BACKGROUND

In general, an anisotropic conductive films (ACF) containing conductiveparticles is widely used when an electronic component such as anintegrated circuit is mounted on a substrate in COG (Chip on Glass)connection for connecting an integrated circuit directly to a glasssubstrate such as a liquid-crystal display or FOG (Film on Glass)connection for connecting a flexible printed board to a glass substrateof a flat panel display. The anisotropic conductive film is athermosetting resin film with fine conductive particles dispersedtherein. By interposing the anisotropic conductive film between alignedelectrodes and performing thermal compression, the conductive particlespositioned between the electrodes can form a conductive route. On theother hand, insulation properties of the thermosetting resin can reducea short circuit between electrodes adjacent in a substrate surfacedirection. That is, the anisotropic conductive film has anisotropy offorming conductivity in a pressurizing direction (direction of both ofthe electrodes) and insulation properties are kept in a non-pressurizingdirection (surface direction of the substrate). Having thesecharacteristic, the anisotropic conductive film can collectively connecta plurality of electrodes provided on an integrated circuit, printedboard, glass substrate, or the like, and can retain insulationproperties of adjacent electrodes in the substrate surface direction.

However, with high fineness and high density of connection circuits inelectronic devices in recent years, reliability of connection using theanisotropic conductive film matters. That is, when the size of anelectrode as a connection target decreases, the number of conductiveparticles contributing to conductivity between paired electrodesdecreases, and connection reliability between the electrodes may not besufficiently obtained. Moreover, when a space between electrodesadjacent in the substrate surface direction is narrowed, both of theadjacent electrodes and the conductive particles may be in contact witheach other, and insulation reliability may not be sufficiently obtained.Thus, for example, an anisotropic conductive film in a state withconductive particles dispersed by means such as application of amagnetic field and as being separated from other conductive particles isdisclosed (for example, refer to Japanese Unexamined Patent ApplicationPublication No. 2015-167106).

SUMMARY

A method for manufacturing connection structure according to anembodiment of the present invention, the method includes arrangingconductive particles and a first composite on a first electrode locatedon a first surface of a first member, arranging a second composite onthe first electrode and a region other than the first electrode of thefirst surface, arranging the first surface and a second surface of asecond member where a second electrode is located, so that the firstelectrode and the second electrode are opposed to each other, pressingthe first member and the second member, and curing the first compositeand the second composite.

A connection structure according to an embodiment of the presentinvention includes a first member having a first surface, a firstelectrode located on the first surface, a second member having a secondsurface opposed to the first surface, a second electrode opposed to thefirst electrode and located on the second surface, a first resin andconductive particles arranged between the first electrode and the secondelectrode, and a second resin arranged between the first electrode andthe second electrode and between a region other than the first electrodeon the first surface and a region other than the second electrode on thesecond surface. The first resin is in contact with the first electrode,the second resin is in contact with the second electrode, and the firstin and the second resin is different compositions from each other.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1A to FIG. 1E shows a configuration of a connection structureaccording to an embodiment of the present invention;

FIG. 2A to FIG. 2C shows method for producing the connection accordingto an embodiment of the present invention;

FIG. 3A to FIG. 3C shows a method for producing connection structureaccording to an embodiment of the present invention;

FIG. 4A to FIG. 4C shows a method for producing the connection structureaccording to an embodiment present invention;

FIG. 5A to FIG. 5E shows a method for producing the connection structureaccording to an embodiment of the present invention;

FIG. 6A to FIG. 6F shows a method for producing the connection structureaccording to an embodiment of the present invention;

FIG. 7A to FIG. 7C shows a configuration of a connection structureaccording to an embodiment of the present invention;

FIG. 8A to FIG. 8F shows a method for producing the connection structureaccording to an embodiment of the present invention;

FIG. 9A to FIG. 9E shows method for producing the connection structureaccording to an embodiment of the present invention;

FIG. 10A to FIG. 10C shows a configuration of a connection structureaccording to an embodiment of the present invention;

FIG. 11A to FIG. 11C shows a method for producing the connectionstructure according to an embodiment of the present invention;

FIG. 12A to FIG. 12C shows a method for producing the connectionstructure according to an embodiment of the present invention;

FIG. 13A to FIG. 13C shows a method for producing the connectionstructure according to an embodiment of the present invention;

FIG. 14A to FIG. 14E shows a method for producing the connectionstructure according to an embodiment of the present invention;

FIG. 15A to FIG. 15F shows a method for producing the connectionstructure according to an embodiment of the present invention;

FIG. 16A to FIG. 16C shows a configuration of a connection structureaccording to an embodiment of the present invention;

FIG. 17A to FIG. 17E shows a method for producing the connectionstructure according to an embodiment of the present invention;

FIG. 18A to FIG. 18F shows a method for producing the connectionstructure according to an embodiment of the present invention;

FIG. 19A and FIG. 19B shows an example of the connection structureaccording to an embodiment of the present invention;

FIG. 20A and FIG. 20B shows an example of the connection structureaccording to an embodiment of the present invention;

FIG. 21A and FIG. 21B shows an example of the connection structureaccording to an embodiment of the present invention;

FIG. 22A and FIG. 22B shows an example of the connection structureaccording to an embodiment of the present invention;

FIG. 23A and FIG. 23B shows an example of the connection structureaccording to an embodiment of the present invention;

FIG. 24A and FIG. 24B shows an example of the connection structureaccording to an embodiment of the present invention; and

FIG. 25A and FIG. 25B shows an example of the connection structureaccording to an embodiment of the present invention.

DESCRIPTION OF EMBODIMENTS

Hereinafter, embodiments of the present invention will be described withreference to the drawings and the like. The present invention may becarried out in various embodiments, and should not be construed as beinglimited to any of the following embodiments. In the drawings, componentsmay be shown schematically regarding the width, thickness, shape and thelike, instead of being shown in accordance with the actual sizes, forthe sake of clear illustration. The drawings are merely examples and donot limit the present invention in any way. In the specification and thedrawings, components that are substantially the same as those describedor shown previously bear the identical reference signs thereto (or theidentical reference signs followed by letters “a”, “b” or the like), anddetailed descriptions thereof may be omitted. The terms “first”,“second” and the like used for elements are merely provided fordistinguishing the elements and do not have any other significanceunless otherwise specified.

In the specification and the claims, an expression that a component is“on” the other component encompasses a case where such a component is incontact with the other component and also a case where such a componentis above or below the other component, namely, a case where stillanother in component is provided between such a component and theanother component, unless otherwise specified.

In the anisotropic conductive film, since the sequence of the conductiveparticles is irregularly disturbed when substrates are subjected tothermal compression. Thus, it is difficult to sufficiently solveproblems such as conduction failure due to the absence of conductiveparticles between the electrodes and a short circuit due to a contact ofthe conductive particles between the adjacent electrodes. Moreover, witha heat curing connection scheme, a dimensional change occurs inprinciple, due to a difference in coefficient of thermal expansionbetween upper and lower substrates, and a problem of deviation occursbetween the electrodes formed on the upper and lower substrates. Inseveral embodiments described further below, one aspect of a connectionstructure capable of solving one or plurality of these problems isdescribed.

In the specification, a connection structure in COG connection forconnecting an integrated circuit (second electronic component) to aglass substrate of a liquid-crystal display (a first electroniccomponent) is described by way of example. However the connectionstructure is not limited to this, and may be a connection structure inFOG connection for connecting a flexible printed board to a glasssubstrate of a flat panel display. In this case, the second electroniccomponent may be a flexible printed board such as a TAB (Tape AutomatedBonding) or COF (Chip on film).

First Embodiment Configuration of Connection Structure

FIG. 1A to FIG. 1D shows the configuration of a connection structureaccording to one embodiment of the present invention. FIG. 1A is a planview of the connection structure according to one embodiment of thepresent invention. FIG. 1B is a sectional view along an A-A′ line ofFIG. 1A. FIG. 1C is an enlarged sectional view of a conductive particlein a region B of FIG. 1B.

As shown in FIG. 1A and FIG. 1B, first electronic component 101 includesa terminal 104, a first insulating film 106, a second insulating film108, and a first electrode 110 on a connection surface (first surface)of a first member 102. On the connection surface (first surface) of thefirst electronic component 101, a second electronic component 111 ismounted. The second electronic component 111 includes a second electrode114 on a connection surface (second surface) of a second member 112. Thefirst surface of the first electronic component 101 and the secondsurface of the second electronic component 111 are arranged so as to beopposed to each other. The connection structure 100 serves a function ofphysical connection between the first electronic component 101 and thesecond electronic component 111 and electrical connection between thefirst electrode 110 and the second electrode 114. The connectionstructure 100 includes the first member 102 having the first surface,the first electrode 110, the second member 112 having the secondsurface, the second electrode 114, conductive particles 10, a firstresin 20, and a second resin 30.

A plurality of first electrodes 110 arranged on the first surface of thefirst member 102. On the first surface of the first member 102, a secondinsulating film 108 is arranged in a region other than a region wherethe first electrodes 110 are arranged. A plurality of second electrodes114 are arranged on the second surface of the second member 112 so as tocorrespond to the plurality of first electrodes 110. On the secondsurface of the second member 112 an insulating film may be arranged in aregion other than a region where the second electrodes 114 are arranged.

The plurality of first electrodes 110 and the plurality of secondelectrodes 114 are arranged so as to be the first electrode 110 and thesecond electrode 114 are opposed to each other. The plurality ofconductive particles 10, the first resin 20, and the second resin 30 arearranged between the opposing first electrode 110 and second electrode114. The plurality of conductive particles 10 are arranged in a surfacedirection (D2-D3 surface direction) between the opposing first electrode110 and second electrode 114. One conductive particle 10 is arrangedbetween the opposing first electrode 110 and second electrode 114 in anopposing direction (D1 direction) of the first electrode 110 and thesecond electrode 114. Each of the plurality of conductive particles 10are in contact with the opposing first electrode 110 and secondelectrode 114. As shown in FIG. 1C, the conductive particle 10 ispressured and deformed in the opposing direction (D1 direction) betweenthe first electrode 110 and the second electrode 114 by a method formanufacturing connection structure, which will be described furtherbelow. That is, a distance between the first electrode 110 and thesecond electrode 114 in the opposing direction (D1 direction) of theelectrodes is substantially equal to the height of the conductiveparticle 10 in the opposing direction (D1 direction) of the electrodes.The height of the conductive particle 10 in the opposing direction (D1direction) of the electrodes is pressured and deformed by approximately10% to 40%. With a stress provided among the first electrode 110, theconductive particles 10, and the second electrode 114, the first resin20 and the second resin 30 are eliminated at the contact part betweenthe first electrode 110 and the conductive particle 10 and the contactpart between the second electrode 114 an the conductive particle 10.Furthermore, even natural oxide film is formed on the first electrode110, the conductive particle 10, or the second electrode 114 and itssurface is insulated the first electrode 110 and the second electrode114 are pressure-welded with the conductive particle 10 interposedtherebetween, thereby breaking the natural oxide film to form aconductive route. Furthermore, deformation of the conductive particle 10can increase the area of contact between the first electrode 110 and theconductive particle 10 and the area of contact between the secondelectrode 11 and the conductive particle 10. This arrangement allows theconductive particle 10 to electrically connect the first electrode andthe second electrode 114.

The plurality of conductive particles 10 are dispersed in the firstresin 20 and the second resin 30 between the first electrode 110 and thesecond electrode 114. Each of the plurality of conductive particles 10are surrounded by the first resin 20 on the first electrode 110 in thesurface direction (D2-D3 surface direct). Each of the plurality ofconductive particles 10 are surrounded by the second resin 30 on thesecond electrode 114 in the surface direction (D2-D3 surface direction).The first resin 20 and the second resin 30 are insulating resin. Thus,the connection structure 100 has insulation properties in the surfacedirection (D2-D3 surface direction). However, the plurality ofconductive particles 10 arranged between the opposing first electrode110 and second electrode 114 and adjacent to each other in the surfacedirection (D2-D3 surface direction) may be in contact with each other.When the conductive particles 10 adjacent to each other in the surfacedirection (D2-D3 surface direction) are in contact with each other, theconductive particles 10 adjacent to each other are also electricallyconnected. This arrangement allows the conductive particles 10 tofurther reliably connect the opposing first electrode 110 and secondelectrode 114 electrically. The distance between the adjacent conductiveparticles 10 can be appropriately controlled according to theconcentration of the conduct particles 10 mixed into a first composite20′, which be described further below.

As shown in FIG. 1A and FIG. 1B, the plurality of conductive particles10 and the first resin 20 are arranged on an upper surface of the firstelectrode 110. The plurality of conductive particles 10 and the firstresin 20 are arranged in each certain region when viewed in the opposingdirection (D1 direction) of the electrodes. In the present embodiment,the diameter of the conductive particle 10 when viewed in the opposingdirection (D1 direction) of the electrodes is in a range between a valueequal to or larger than 2 μm and a value equal to or smaller than 10 μm.The number of regions where the conductive particles 10 and the firstresin 20 are arranged on the upper surface of one first electrode 110 isone or more, and the regions are preferably separated from each other by5 μm. The number of conductive particles 10 in one region where theconductive particles 10 and the first resin 20 are arranged ispreferably equal to or larger than one and equal to or smaller thanseven. The number of conductive particles 10 arranged in one region ispreferably seven, and more preferably three. When viewed in the opposingdirection (D1 direction) of the electrodes, the number of conductiveparticles 10 arranged between the opposing first electrode 110 andsecond electrode 114 is preferably in a range between a value equal toor larger than seven per 400 μm² and, a value equal to or smaller thantwenty per 400 μm². When the number of conductive particles 10 issmaller than seven per 400 μm², the connection resistance value may tendto vary. When the number of conductive particles 10 is larger thantwenty per 400 μm², the pressure deformation amount of the conductiveparticles 10 may be decreased due to load dispersion, causing thenatural oxide film to be unable to be broken at a connection region andincreasing connection resistance. Furthermore, when the number ofconductive particles 10 is larger than twenty per 400 μm², the pressuredeformation amount tends to change with time, and connection resistancetends to change with time. The above-described arrangement allows theconductive particles 10 to reliably connect the opposing first electrode110 and second electrode 114, and can prevent short circuit between theplurality of first electrodes 110 adjacent to each other in the surfacedirection (D2-D3 surface direction), between the plurality of secondelectrodes 114 adjacent to each other in the surface direction (D2-D3surface direction), and between the first electrode 110 and the secondelectrode 114 not opposed to each other.

In the present embodiment, shape of the region where the conductiveparticles 10 and the first resin 20 are arranged when viewed in theopposing direction (D1 direction) of the electrodes is a circle.However, the shape is not limited to this, and the region where theconductive particles 10 and the first resin 20 are arranged may have anyshape satisfying the above-described condition. In the presentembodiment, the region where the conductive particles 10 and the firstresin 20 are arranged is positioned at two locations on the uppersurface of one first electrode 110. Also, seven conductive particles 10are arranged in one region. However, this is not meant to berestrictive, and the number of regions where the conductive particles 10and the first resin 20 are arranged on the upper surface of one firstelectrode 110 can be adjusted as appropriate to satisfy theabove-described condition, depending on the area of the upper surface ofthe first electrode 110 the area of the region where the conductiveparticles 10 and the first resin 20 are arranged, and the size of theconductive particles 10. Also, the number of conductive particles 10arranged in one region can be adjusted as appropriate to satisfy theabove-described condition, depending on the size the conductiveparticles 10 and concentration of the conductive particles 10 mixed intothe first composite 20′.

The second resin 30 is arranged between the first surface of the firstmember 102 and the second surface of the second member 112. The secondresin 30 is arranged in a region not between the opposing firstelectrode 110 and second electrode 114. The second resin 30 is arrangedbetween a region other than the first electrode of the first surface anda region other than the second electrode of the second surface. That is,the second resin 30 is arranged between the plurality of firstelectrodes 110 adjacent to each other in the surface direction (D2-D3surface direction) and on the periphery thereof (between the pluralityof second electrodes 114 adjacent to each other in the surface direction(D2-D3 surface direction) and on the periphery thereof). Furthermore,the second resin 30 is also arranged between the first electrode 110 andthe second electrode 114 and in a region other than the region where theconductive particles 10 and the first resin 20 are arranged. The secondresin 30 is arranged between the regions adjacent in the surfacedirection (D2-D3 surface direction) where the plurality of conductiveparticles 10 and the first resin 20 are arranged and on the peripherythereof. In other words, the conductive particles 10 and the first resin20 are surrounded by the second resin 30 in the surface direction (D2-D3surface direction). That is, when viewed in the opposing direction (D1direction) of the electrodes, the plurality of conductive particles 10are surrounded by the first resin 20, and the first resin 20 issurrounded by the second resin 30 on the first surface of the fireelectronic component 101. As shown in FIG. 1B and FIG. 1C, the secondresin 30 is also arranged between the first electrode 110 and the secondelectrode 114 in the region where the conductive particles 10 and thefirst resin 20 are arranged. The second resin 30 is arranged between thefirst resin 20 and the second electrode 114. That is, when viewedopposing direction (D1 direction) of the electrodes, the plurality ofconductive particles 10 are surrounded by the second resin 30 on thesecond surface of the second electronic component 111. The second resin30 is an insulating resin. Thus, the connection structure 100 hasinsulation properties in the surface direction (D2-D3 surfacedirection). This arrangement allows the second resin 30 to reliablyinsulate between the plurality of first electrodes 110 adjacent in thesurface direction (D2-D3 surface direction), between the plurality ofsecond electrodes 114 adjacent in the surface direction (D2-D3 surfacedirection), and between the first electrode 110 and the second electrode114 not opposed to each other.

The first resin 20 and the second resin 30 are arranged between thefirst electrode 110 and the second electrode 114. The first resin 20 isarranged so as to be in contact with the first electrode 110, and thesecond resin 30 is arranged so as to be in contact with the secondelectrode 114. That is, the first resin 20 and the second resin 30 arein contact in the surface direction (D2-D3 surface direction) betweenthe first electrode 110 and the second electrode 114, and are laminatedin the opposing direction (D1 direction) of the electrodes.

The boundary between the first resin 20 and the second resin 30 can beobserved by cross-sectional observation of the connection structure 100.From a difference in composition between the first resin 20 and thesecond resin 30 the boundary between the first resin 20 and the secondresin 30 can also be determined by a process/observation apparatus suchas a Focused Ion Beam (FIB) process observation apparatus, a ScanningElectron Microscope (SEM), or a Transmission Electron Microscope (TEM).

If the first composite 20′ and a second composite 30′, which will bedescribed further below, are less phase-soluble, the boundary betweenthe first resin 20 and the second resin 30 can be observed as aninterface. If the first composite 20′ and a second composite 30′ aresimilar to each other in composition and the interface therebetweendisappear in a process described further below, the boundary may beobserved as a boundary layer with the first resin 20 and the secondresin 30 mixed together.

The first electronic component 101 may be, for example, a flat displaysuch as a liquid-crystal display, an organic EL display, or a plasmadisplay, and the first member 102 is preferably an insulating substratesuch as, for example, a glass substrate or a transparent film substrate.The first electrode 110 corresponds to, for example, an externalconnection terminal provided to a display. The first electrode 110 andthe terminal 104 may be formed of a transparent conductive material suchas ITO (indium tin oxide) or IZO (indium zinc oxide); a metal such ascopper (Cu), aluminum (Al), molybdenum (Mo), or titanium (Ti); an alloyincluding at least one type thereof (such as Mo—Ti alloy); or alaminated structure of these materials (such as Mo/Cu laminatedstructure, Mo—Ti alloy/Cu laminated structure, Mo/Al laminatedstructure, Mo/Al/Mo laminated structure, or Al/Ti laminated structure).

The second electronic component 111 may be a Si chip having anintegrated circuit formed thereon. In this case, the second electrode114 corresponds to an external connection terminal (bonding pad)provided to the integrated circuit. The second member 112 is preferablya silicon substrate, a SiC substrate, a sapphire substrate, a plasticsubstrate, or the like. The second electrode 114 is preferably formed,for example, of gold (Au) or by plating a surface of copper (Cu) withgold. When the second electronic component 111 is, for example, aflexible printed board, the second member 112 is preferably, forexample, an insulating polymer film made of a polyimide, a para-basedpolyamide, or the like. The second electrode 114 corresponds to anexternal connection terminal provided to, for example, the flexibleprinted board is generally formed of copper (Cu), and has its surfaceplated with gold.

The size of each of the first electrode 110 and the second electrode 114when viewed in the opposing direction (D1 direction) is not limited toparticular sizes. The distance between the pluralities of firstelectrodes 110 adjacent in the surface direction (D2-D3 surfacedirection) (the distance between the pluralities of second electrodes114 adjacent in the surface direction) is not limited to particularvalues, and is, for example, at least equal to or large than 5 μm. Thisconfiguration allows the first electrode 110 and the second electrode114 to be electrically connected without impairing insulationproperties. In the present embodiment, the first electrode 110 and thesecond electrode 114 are arranged so that short sides thereof arealigned in a line at one end part of each of the first electroniccomponent 101 and the second electronic component 111. However, this notmeant to be restrictive, and a plurality of rows of the first electrodes110 and the second electrodes 114 may be arranged, and the firstelectrodes 110 and the second electrodes 114 may be arranged in astaggered formation.

The conductive particle 10 included in the connection structure 100 maybe in an oblate spheroidal shape. The diameter (longitudinal diameter)of the conductive particle 10 when viewed in the opposing direction (D1direction) of the electrodes is in a range between a value equal to orlarger than 2 μm and a value equal to or smaller than 10 μm. Theconductive particle 10 may originally have a spherical shape with theabove-described longitudinal diameter as a diameter, and may be deformedto be flat in the opposing direction (D1 direction) of the electrodes bya range between a value equal to or larger than 10% and a equal to orsmaller than 40% with respect to 100% of the longitudinal diameter. Thediameter (longitudinal diameter) and the pressure deformation amount ofthe conductive particle 10 can be selected as appropriate from thevalues in the above-described range, depending on the type of the firstelectronic component 101 and the second electronic component 111, themethod for manufacturing each connection structure, and so forth. Whilethe conductive particle 10 has a round shape in the present embodimentas shown in FIG. 10, this is not meant to be restrictive and, forexample, as shown in FIG. 1E, the conductive particle 10 may have aspherical shape with a plurality of protrusions on its surface (aconfeito shape). This is more preferable because, with the surface ofthe spherical shape having a fine convex configuration, the naturaloxide film in the connection region can be broken, for example.

The material of the conduct particle 10 is not limited to particularmaterials, and any can be selected as appropriate for use from knownconductive particles. The conductive particle 10 may be a metal-coatedparticle by coating with metals 10 b and 10 c such as nickel (Ni),copper (Cu) or gold (Au), a particle core with a highly-hard resinmaterial coated with a rubber-like elastic resin or a particle core 10 awith a highly-hard inorganic material coated with a rubber-likeinorganic elastic body, as shown in FIG. 1D and FIG. 1E. In metalcoating, a Ni/Cu laminated structure, a Ni/Au laminated structure, or aCu/Au laminated structure may be formed by, for example, barrelsputtering, metal nanoparticle plating, electroless plating, ultrasonicplating, or the like.

The first resin 20 and the second resin 30 are formed by curing thefirst composite 20′ and the second composite 30′ including differentmaterials. The materials of the first composite 20′ and the secondcomposite 30′ are not limited to particular materials, and any can beselected as appropriate from known curable resin materials. In thepresent embodiment, the curable ream materials of the first composite20′ and the second composite 30′ both contain a radical-polymerizationresin. As the radical-polymerization resin, a (meth)acrylic monomer or(meth)acrylate oligomer is preferable, and one bonded in an ester formis more preferable. The (meth)acrylate oligomer has at least one(meth)acryloyl group or more and for example, epoxy acrylate, urethaneacrylate, polyester acrylate, polybutadiene acrylate, polyol acrylatepolyether acrylate silicone resin acrylate, melamine acrylate, or thelike can be used. The (meth)acryl oligomer may be monofunctional orpolyfunctional, and preferably contains a polyfunctional monomer oroligomer. The curably resin material may be configured by selecting twoor more types from (meth)acrylate monomers and (meth)acrylate oligomers.

In particular, as a curable resin material of the second composite 30′,one with a low volume shrinkage ratio at the time of curing ispreferable. Thus, the (meth)acrylic monomer may contain, for example, anamide methylol structure portion, and may contain a dendrimer or hyperbranch polymer structure portion. In a (meth)acrylic monomer compoundhaving an amide methylol structure portion, together with polymerizationof carbon-carbon double bonds derived from (meth)acrylic acid,methylene-oxygen bonds in the amide methylol structure portion arecleaved at the time of photocuring. Thus, with the second compound 30′containing a (meth)acrylic monomer compound having at least one amidemethylol structure portion formed of —CO—NH—CH₂—O— in a molecule as acurable component, the volume shrinkage ratio of the second resin 30 dueto curing of the second composite 30′ can be more reduced, and warpagedue to a difference in flexural rigidity between the first electroniccomponent 101 and the second electronic component 111 can be reduced.With a branch including a dendrimer or hyperbranch polymer structureportion having an aryl group, a Van der Waals distance between branchesbecomes shorter than a Van der Waals distance between general molecules.Thus, with the second composite 30′ containing a dendrimer orhyperbranch polymer structure portion having an acryl group as a curablecomponent, the volume shrinkage ratio of the second resin 30 due tocuring of the second composite 30′ can be more reduced, and warpage dueto a difference in flexural rigidity between the first electroniccomponent 101 and the second electronic component 111 can be reduced.

As the curable resin material of the second composite 30′, afluorene-based acrylate is preferably used. The second composite 30′ maycontain an ene/thiol-based curable resin containing a composite havingan ethylene unsaturated double bond and a thiol compound a curablecomponent, at least one of these components may contain a compoundhaving a 9,9-bisarylfluorene skeleton. The 9,9-bisarylfluorene compoundmay be a 9,9-bisarylfluorene compound having an ethylene unsaturatedbond and/or a 9,9-bisarylfluorene compound having a mercapto group. Asthe ethylene unsaturated compound, for example,9,9-bis(4-acryloyloxyethoxyphenyl)fluorene (produced by Osaka GasChemicals Co., Ltd., OGSOL EA-0200) and phenoxyethyl acrylate (producedby KYOEISHA CHEMICAL CO., LTD., LIGHT ACRYLATE POA) may be used. As thethiol compound, for example, pentaerythritol tetra (3-mercaptobutyrate)(produced by SHOWA DENKO K. K., Karenz MT PE1) may be used. With thesecond composite 30′ containing this curable resin material, the volumeshrinkage ratio of the second resin 30 due to curing of the secondcomposite 30′ can be more reduced, and warpage due to a difference inflexural rigidity between the first electronic component 101 and thesecond electronic component 111 can be reduced.

As the curable resin material the second composite 30′, an ene compoundhaving in a molecule two or more functional groups selected from a groupof an allyl ether group, a vinyl ether group, an acrylate group, and amethacrylate group or ene compound as a mixture of two or more types ofthe above-described ene compounds, and a substance obtained byperforming oxidizing-compound-process on the ene/thiol-based curableresin containing a thiol compound having two or more thiol groups in onemolecule may be used. A compound having two or more mercapto groups inone molecule may contain esters obtained from mercaptocarboxylic acidand polyhydric alcohol, aliphatic polythiols, aromatic polythiols, andother polythiols, or one, two or more of these may be used. Theoxidizing-compound process is preferably performed with a gas havingoxidative capacity. The gas having oxidative capacity is a compoundhaving air properties and oxidative capacity under temperature andatmospheric conditions for performing oxidizing-compound process. As thegas having oxidative capacity, air, oxygen, ozone, or the like can beused, and a mixture gas partially containing any of these may be used.The second composite 30′ can enhance stability with time by performingoxidizing-compound process on the above-described photocurable resinmaterial.

The materials of the first composite 20′ and the second composite 30′further contain a photocuring initiating component. The photocuringinitiating component is a photoradical initiator, and may be anycompound which generates radicals by irradiating ultraviolet rays orvisible, rays. As an ultraviolet-ray radical, initiator, for example, anacetophenone-based initiator, a benzoin-ether-based initiator, abenzophenone-based initiator, an α-diketone-based initiator, athioxanthone-based initiator, or the like can be used. As a visible-rayradical initiator, for example, a camphorquinone-based compound, anacylphosphine oxide compound, or the like can be used. Also, oneclassified as an ultraviolet-ray radical initiator but capable ofvisible-ray radical initiation by using combination with a sensitizermay be used. The sensitizer can be appropriately used as required. Asthe sensitizer, a known composite can be used. For example, anamine-based compound, a (meth)acrylic acid ester of an alkanol amine, orthe like can be used. A plurality of types of the photocuring initiatingcomponent and the sensitizer can be used in combination. For example, byusing an ultraviolet-ray radical initiator and a visible-ray radicalinitiator in combination, a curable wavelength region can be expanded.The photocuring initiating component is more preferably a photoradicalinitiator which generates radicals with a irradiation light in a rangeof wavelength between a value equal to or larger than 300 nm and a valueequal to or smaller than 500 nm. The photocuring initiating component iscompounded in the curable resin material so that the curable resinmaterial can be curing at room temperatures with a light irradiation fora period of preferably equal to or shorter than approximately threeseconds, more preferably equal to or shorter than one second. Thecurable resin material is selected as appropriate so as to allow curingat room temperatures with the above-described time period.

In the present embodiment, the first composite 20′ and the secondcomposite 30′ more preferably further on in a shielding part curableactivation compound such as, for example, a chain transfer agent. Thechain transfer agent transmits radicals generated by light irradiationto a shielding part which light does not directly reach. As the chaintransfer agent, for example, a compound containing at least one or moreof selected from a urethane bond, a bond, and an isocyanate group andone or more of alkoxysilyl group can be used. In photocuring reactionusing the above-described chain transfer agent, polyalcohol having ahydroxyl group as one type of anion is generated as a by-product. Withthis polyalcohol and the alkoxysilyl group containing in the chaintransfer agent undergoing a transesterification, curing furtherproceeds. That is, with the chain transfer agent being contained in thefirst composite 20′ the second composite 30′, radical curing and anioncuring occur simultaneously, thereby allowing curing of the shieldingpart where light does not directly reach.

With the first composite 20′ and the second composite 30′ containing ashielding part curable activation compound, the first composite 20′ andthe second composite 30′ can be reliably cured even under conditionswith the connection method, the material of the first electroniccomponent 101, the second electronic component 111, the first electrode110, and the second electrode 114, and so forth in which the firstcomposite 20′ and the second composite 30′ cannot be cured only with theaction of photocuring initiating component by light irradiation.

In the present embodiment, the material of the first composite 20′ mayfurther contain an anaerobic curing initiating component. As theanaerobic curing initiating component, a known group including organicperoxide and a curing accelerator can be used. As the organic peroxide,for example, any of hydroperoxides, ketone peroxides, diallyl peroxides,peroxyesters, and so forth can be used. As the curing accelerator, forexample, an o-benzoic sulfimide (saccharin), a hydrazine compound, anamine compound, a mercaptan compound, or the like can be used. Aplurality of types of the anaerobic curing initiation component and thecuring accelerator may be used in combination.

In the present embodiment, the first composite 20′ is surrounded by thefirst surface (including the first electrode 110), the second surface(including the second electrode 114), and the second composite 30′.Furthermore, the first composite 20′ is in contact with the firstelectrode 110, the second electrode 114, and the conductive particles10. The first electrode 110, the second electrode 114, and theconductive particles 10 contain transition metals. Thus, with the firstcomposite 20′ containing an anaerobic curing initiating component, aredox reaction by the cure acceleration agent and the transition metalions dissolves peroxide, thereby allowing anaerobic curing of the firstcomposite 20′ to be initiated.

With the first composite 20′ further containing an anaerobic curinginitiating component, the first composite 20′ can be reliably cured evenunder conditions with the connection method, the material of the firstelectronic component 101, the second electronic component 111, the firstelectrode 110, and the second electrode 114, and so forth in which thefirst composite 20′ cannot be cured only with the action of aphotocuring initiating component by light irradiation.

The additive can be appropriately used as required to improve or modifythe properties such as fluidity, coating characteristics,preservability, curing characteristics, and physical properties aftercuring. As the additive, any known compound can be used. Examples of theadditive include a silane coupler, a diluent, a modifying agent, asurface active agent, a preservative stabilizer, an antiforming agent,and a leveling agent, although not limited thereto. The silane coupleris not limited to particular agent and for example, any of epoxy-based,amino-based, mercapto/sulfide-based, and ureido-based ones and so forthcan be used. With the addition of silane coupler, adhesion at theinterface between the organic material and the inorganic material isimproved.

The viscosity of the first composite 20′ is higher than the viscosity ofthe second composite 30′. The viscosity of the first composite 20′ is ina range between a value equal to or higher than 5×10³ cP and a valueequal to or lower than 5×10⁵ cP. The viscosity of the second composite30′ is in a range between a value equal to or higher than 2×10³ cP and avalue equal to or lower than 2×10⁵ cP. It is required that the viscosityof the first composite 20′ is twice as high as the viscosity of thesecond composite 30′ or higher. The viscosity of the first composite 20′and the second composite 30′ can be controlled also by the degree ofpolymerization of the resin material contained in the first composite20′ and the second composite 30′. The viscosity of each composite can beselected as appropriate from values within the above-described range,depending on the type of the first electronic component 101 and thesecond electronic component 111, the method for manufacturing connectionstructure, the method for composite arrangement, and so forth. If theviscosity of the first composite 20′ is lower than 5×10³ cP, uniformdispersibility of the conductive particles 10 in the first composite 20′is degraded, and sedimentation and agglomeration tend to occur. With theviscosity of the first composite 20′ being higher than the viscosity ofthe second composite 30′, the conductive particles 10 mixed into thefirst composite 20′ is inhibited from flowing, and can be efficientlyarranged between the first electrode 110 and the second electrode 114.Therefore, connection reliability between the first electrode 110 andthe second electrode 114 can be ensured.

The first resin 20 and the second resin 30 are formed by curing thefirst composite 20′ and the second composite 30′. The volume shrinkageratio of the first resin 20 due to curing of the first composite 20′ andthe volume shrinkage ratio of the second resin 30 due to curing of thesecond composite 30′ are both preferably equal to or smaller than 4%,and more preferably equal to or smaller than 2%. If the volumeshrinkages ratio of the first resin 20 and the second resin 30 arelarger than 4%, an inner shrinkage stress occurs, warpage due to adifference in flexural rigidity between the first electronic component101 and the second electronic component 111 tends to occur, and physicalconnection reliability between the first electronic component 101 andthe second electronic component 111 is degraded.

The first resin 20 more preferably has high power of adhesion to aconductive material such as a metal material or metal oxide material.The first resin 20 preferably has high power of adhesion to a metalmaterial forming the first electrode 110 and the second electrode 114,and preferably has high power of adhesion to, for example, Au, ITO, andso forth. The second resin 30 preferably has high power of adhesion to aresin material. The second resin 30 preferably has high power ofadhesion to an insulating film material forming the first surface of thefirst member 102 and the second surface of the second member 112, andpreferably has high power of adhesion to an insulating material such as,for example, polyimide, para-based polyamide film, P—SiNx, glass, and soforth. The adhesion power of the first resin 20 is preferably in a rangeequal to or larger than 500 N/m. The adhesion power of the second resin30 is preferably in a range equal to or larger than 700 N/m. Theadhesion power, glass transition temperature, and hardness of each resincan be selected as appropriate, depending on the type of the firstelectronic component 101 and the second electronic component 111, themethod for manufacturing connection structure, and so forth. With thefirst resin 20 and the second resin 30 each being selected depending onthe material of an adherend, the adhesive power between the firstsurface of the first member 102 and the second surface of the secondmember 112 can be further improved. Therefore, physical connectionreliability between the first electronic component 101 and the secondelectronic component 111 can be improved.

The Method for Manufacturing Connection Structure

Next, a method for manufacturing connection structure according to oneembodiment of the present invention is described by using FIG. 2A toFIG. 5E. Since the existing first electronic component 101 and secondelectronic component 111 can be used in the present embodiment, theirdescription is omitted. In FIG. 2A to FIG. 5E, the method of forming theconnection structure 100 is described in detail.

First, the plurality of conductive particles 10 and the first composite20′ are arranged in a predetermined region on the first electrode 110.The plurality of conductive particles 10 and the first composite 20′ aremixed, and are arranged by using an offset printing scheme. Since themixture of the conductive particles 10 and the first composite 20′contains the conductive particles 10, a pad printing scheme oftransferring a printed matter by using a pad is particularly preferable.By using FIG. 2A to FIG. 5E, a method of arranging the plurality ofconductive particles 10 and the first composite 20′ is described.

FIG. 2A to FIG. 2 show a process of arranging the plurality ofconductive particles 10 and the first composite 20′ on a plate 220. FIG.3A to FIG. 3C are sectional views along a C-C′ line of FIG. 2A to FIG.2C. In the present embodiment, the plate 220 is, for example, awaterless planographic plate. The plate 220 has depressed parts 226corresponding to regions where the plurality of conductive particles 10and the first composite 20′ are arranged on the first surface of thefirst member 102. The plate 220 includes a lyophilic layer 222 and aliquid-repellent layer 224. The liquid-repellent layer 224 is arrangedas a liquid contact surface, and has an opening. The liquid-repellentlayer 224 exposes the lyophilic layer 222 at a bottom surface of theopening. That is, the liquid-repellent layer 224 having the opening isarranged on an upper ace of the plate 220, and the lyophilic layer 222is arranged under the liquid-repellent layer 224. The depressed parts226 are formed by the opening of the liquid-repellent-layer 224 and thelyophilic layer 222 at the bottom surface of the opening.

The material the lyophilic layer 222 may be, for example, an aluminumoxide (Al₂O). The material of the liquid-repellent layer 224 ispreferably, for example, an elastic silicone resin. The depressed parts226 have a depth substantially equal to the depth of theliquid-repellent layer 224. The depth of the depressed parts 226 isrequired to be larger than the diameter of the conductive particles 10.The plate 220 may be, in addition to a waterless planographic plate, aglass deep-etch plate, a stainless deep-etch plate, a sapphire deep-etchplate, or a zirconia deep-etch plate. The depressed parts 226 whenviewed from the upper surface of the plate 220 are preferably separatedfrom each other by 5 μm or more. If the depressed parts 226 areseparated from each other by less than 5 μm, the liquid-repellent layer224 which separates the adjacent depressed parts 226 tends to be broken,and durability of the plate 220 may be degraded.

In the present embodiment, the shape of each depressed part 226 whenviewed in the opposing direction (D1 direction) of the electrodes iscircle. Also, the depressed part 226 has the same shape in a depthdirection. That is, the depressed part 226 has a shape obtained bycutting out a cylinder from the plate 220. However, the shape of thedepressed part 226 is not limited to this, and the depressed part 226can take any shape with the depth in the above-described range.

In the present embodiment, the of the conductive particles 10 and thefirst composite 20′ is arranged on the plate 220 by using a roller 210.As shown in FIG. 2A to FIG. 2C and FIG. 3A to FIG. 3C, the roller 210moves as rotating from one end to the other end of the plate 220 so thatan outer peripheral surface of the roller 210 is in contact with theupper surface of the plate 220 (upper surface of the liquid-repellentlayer 224), thereby arranging the conductive particles 10 and the firstcomposite 20′ in the depressed parts 226.

As for the concentration of the conductive particles 10 mixed into thefirst composite 20′, the ratio of the conductive particles 10 to thetotal volume of the conductive particles 10 and the first composite 20′is preferably in a range between a value equal to or larger than 20volume % and a value equal to or smaller than 60 volume %. If the mixingamount of the conductive particles 10 is smaller than 20 volume %, it isdifficult to fill the sufficient number of conductive particles 10 inthe depressed parts 226. If the mixing amount of the conductiveparticles 10 is larger than 60 volume %, operability is degraded, and itis difficult to fill the mixture of the conductive particles 10 and thefirst composite 20′ in the depressed parts 226. By arranging the mixtureof the conductive particles 10 and the first composite 20′ with theroller 210, the conductive particles 10 and the first composite 20′ canbe filled in the depressed parts 226 of the plate 220. Since thedepressed parts 226 have the depth in the above-described range, oneconductive particle 10 can be retained in the depth direction (D1direction) of the depressed parts 226. The number of conductiveparticles 10 arranged in one depressed part 226 is preferably equal toor more than one and equal to or smaller than seven. The number ofconductive particles 10 arranged in one depressed part 226 is preferablyseven and, more preferably three. This arrangement allows the conductiveparticles 10 and the first composite 20′ to be efficiently displaced tothe pad in a process of displacing the mixture of the conductiveparticles 10 and the first composite 20′ to the pad, which will bedescribed further below.

Each depressed part 226 is formed by the opening of the elasticliquid-repellent layer 224. Thus, if the conductive particles 10 makecontact with the liquid-repellent layer 224 as the roller 210 progress,the conductive particles 10 can be retained in the depressed parts 226without damage. Since the depressed parts 226 have the lyophilic layer222 at the bottom, it can retain the first composite 20′. On the otherhand, the liquid-repellent layer 224 arranged on the upper surface ofthe plate 220 makes the first composite 20′ liquid-repellent.

FIG. 4A to FIG. 4C show a process of displacing the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe plate 220 to a pad 230. As shown in FIG. 4A to FIG. 4C, the pad 230is pressed in a direction substantially perpendicular to the plate 220,and is then pulled away in the direction substantially perpendicular tothe plate 220, thereby displacing the conductive particles 10 and thefirst composite 20′ filled in the depressed parts 226 to the pad 230.Since the viscosity of the first composite 20′ is in a range between avalue equal to or higher than 5×10³ cP and a value equal to or lowerthan 5×10⁵ cP, the conductive particles 10 mixed into the firstcomposite 20′ can be retained on the surface of the pad 230.

The material of the pad 230 is preferably, for example, an elasticsilicone resin or the like. The shape of the pad 230 preferably has atleast a convex configuration. The shape of the pad 230 can be selectedas appropriate depending on the shape of the first electronic component101, the plate 220, and the like.

FIG. 5A and FIG. 5B show the process of transferring the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe pad 230 to the first electrode 110. As shown in FIG. 5A and FIG. 5B,the pad 230 is pressed in a direction substantially perpendicular to thefirst electrode 110, and is then pulled away in the directionsubstantially perpendicular to the first electrode 110, therebytransferring the mixture of the conductive particles 10 and the firstcomposite 20′ displaced to the pad 230 onto the first electrode 110. Onthe first surface of the first member 102, the conductive particles 10and the composite 20′ form a convex configuration in the opposingdirection (D1 direction) of the electrodes. The viscosity of the curableresin material of the first composite 20′ is in the range between avalue equal to or higher than 5×10³ cP and a value equal to or lowerthan 5×10⁵ cP. Thus, the conductive particles 10 mixed into the firstcomposite 20′ can be retained on the first electrode 110. The use ofthis method allows the conductive particles 10 and the first composite20′ to be reliably arranged in a predetermined region on the firstelectrode 110.

Next, the second composite 30′ is arranged on the first surface of thefirst member 102. As shown in FIG. 5C, the second composite 30′ isarranged on the first electrode 110 and a region other first electrode110 of the first surface of the first member 102. That is, the secondcomposite arranged on the first electrode 110 in a region other than theregion where the plurality of conductive particles 10 and the firstcomposite 20′ are arranged. Furthermore, the second composite 30′ isarranged on the first electrode 110 and on the region, where theplurality of conductive particles 10 and the first composite 20′ arearranged. That is, the second composite 30′ is arranged on the firstsurface of the first member 102 and on the first electrode 110 and theregion other than the electrode 110. In the present embodiment, secondcomposite 30′ is in a paste form, and is arranged by using an inkjetscheme or jet dispensing scheme. However, the method of arranging thesecond composite 30′ is not limited to this scheme, and any existingmethod can be used. For example, coating by inkjet or a dispenser,screen printing, or the like can be used.

The viscosity of the second composite 30′ is in a range between a valueequal to or higher than 2×10³ cP and a value equal to or lower than2×10⁵ cP. It is required that the viscosity of the first composite 20′is twice as high as high as the viscosity of the second composite 30′ orhigher. This allows a flow of the conductive particles 10 mixed into thefirst composite 20′ to be inhibited, and the conductive particles 10 canbe retained on the first electronic component 101.

Next the second member 112 is mounted on the first surface of the firstmember 102. As shown in FIG. 5D, the first surface of the first member102 and the second surface of the second member 112 are arranged so asto be opposed to each other so that the corresponding plurality of firstelectrodes 110 and the plurality of second electrodes 114 are opposed toeach other. The first member 102 and the second member 112 are pressedso that the first surface of the first member 102 and the second surfaceof the second member 112 are pushed in directions substantiallyperpendicular to the respective surfaces. The first surface of the firstmember 102 and the second surface of the second member 112 arepressure-welded to the conductive particles 10, the first composite 20′,and the second composite 30′. Here, the first composite 20′ arranged onthe first electrode 110 has a viscosity higher than that of the secondcomposite 30′, and is thus retained on the first electrode 110 togetherwith the conductive particles 10. The second composite 30′ arranged tobe aid on the conductive particles 10 and the first composite 20′ on thefirst electrode 110 has a viscosity lower than that of the firstcomposite 20′, and thus mostly moves to a region other than the regionwhere the conductive particles 10 and the first composite 20′ arearranged. That is, with a stress being applied between the first surfaceof the first member 102 and the second surface of the second member 112,most of the second composite 30′ positioned between the second electrode114 and the first composite 20′ moves, and the second composite 30′positioned between the second electrode 114 and the conductive particles10 is eliminated. Furthermore, the first composite 20′ and theconductive articles 10 forming the convex configuration on the firstsurface of the first member 102 are buried by the second composite 30′.

In other words, most of the second composite 30′ is arranged on thefirst surface of the first member 102 in a region other than the regionwhere the plurality of conductive particles 10 and the first composite20′ are arranged (convex configuration). The conductive particle 10arranged on the first electrode 110 are arranged so as to be the secondelectrode 114, and the second composite 30′ is arranged so as to be incontact with a region other than the first electrode 110 on the flatsurface and a region other than the second electrode 114 on the secondsurface.

As shown in FIG. 5E, the first member 102 and the second member 112 arefurther pressed to push the first surface of the first member 102 andthe second surface of the second member 112 in the directionssubstantially perpendicular to the respective surfaces. Here, asufficient pressure is applied to cause the opposing first electrode 110and second electrode 114 to be in contact with upper and lower sides ofone conductive particle 10. The pressure to push the first surface ofthe first member 102 and the second surface of the second member 112 canbe adjusted as appropriate by a repulsive force of the conductiveparticles 10 and elastic forces of the first composite 20′ and thesecond composite 30′.

Here, the conductive particles 10 are pressurized until deformed into anoblate spheroidal shape by receiving pressure from the first electrode110 and the second electrode 114. The pressure deformation amount of theconductive particles 10 is controlled in a range between a value equalto or larger than 10% and a value equal to or smaller than 40% withrespect to a longitudinal diameter the conductive particles 10 of 100%.Here, a stress is applied among the first electrode 110, the conductiveparticles 10, and the second electrode 114, thereby eliminating thefirst composite 20′ and the second composite 30′ between the firstelectrode 110 and the conductive particles 10 and between the secondelectrode 114 and the conductive particles 10. Furthermore, even if anatural oxide film is formed on the first electrode 110, the conductiveparticles 10, or the second electrode 114 to insulate its surface, thefirst electrode 110 and the second electrode 114 are press-welded withthe conductive particles 10 interposed therebetween, thereby breakingthe natural oxide film to form a conductive route. Deformation of theconductive particles 10 can increase the area of contact between thefirst electrode 110 and the conductive particles 10 and the area ofcontact between the second electrode 114 and the conductive particles10. This arrangement allows the conductive particles 10 to electricallyconnect the first electrode 110 and the second electrode 114.

With the first member 102 and the second member 112 pressed, theconnection structure 100 is irradiated with light. The wavelength regionof light is preferably an ultraviolet ray and/or visible ray region. Inparticular, ultraviolet rays are more preferable. The wavelength regionof light can be selected as appropriate depending on the photocuringinitiating component and the like included in the first composite 20′and the second composite 30′. The direction of light irradiation can beselected as appropriate from a first electronic component 101 side or asecond electronic component 111 side, depending on the wavelength regionof light, the materials of the first 102 and the second member 112, andso forth. Also, irradiation of light from both sides is preferable, andirradiation from a side surface without a shielding substance is alsoeffective. The light irradiation time can be selected as appropriatedepending on the photocuring initiating component, the curable resinmaterial, and the like contained in the first composite 20′ and thesecond composite 30′. In general, the light irradiation time ispreferably equal to or shorter than approximately three seconds and,more preferable equal to or shorter than one second. In other words,light irradiation intensity, the photocuring initiating component, thecurable resin material, and so forth are selected as appropriate so thatcuring is achieved at room temperatures within the above-described lightirradiation time.

Light irradiation causes most of the first composite 20′ and the secondcomposite 30′ included in the connection structure 100 to be cured atroom temperatures. However, for example, a portion between the firstelectrode 110 and the second electrode 114 which sufficient light doesnot reach may be insufficiently cured. Thus, the material of the firstcomposite 20′ more preferably contains a shielding part curableactivation compound, an anaerobic curing initiating component, or thelike. By containing a shielding part curable activation compound, ananaerobic curing initiating component, or the like, it is possible topromote curing at room temperatures even in a portion which sufficientlight does not reach. By curing the first composite 20′ and the secondcomposite 30′ the first resin 20 and the second resin are formed. Thisconfiguration allows physical connection between the first surface ofthe first runic component 101 and the second surface of the secondelectronic component 111.

According to the present embodiment, a connection structure and a methodfor manufacturing connection structure can be provided can ensureconductivity between the opposing electrodes with a simple process andcan reduce a short circuit between adjacent connection electrodes, evenif the electrodes arranged on the electronic components have highfineness and high density. Furthermore, since no heat curing connectionscheme is used, the electrodes of the upper and lower substrates havingdifferent coefficients of thermal expansion can be connected with highaccuracy.

Second Embodiment

The configuration of a connection structure according to a secondembodiment is the same as the configuration of the connection structureaccording to the first embodiment. A method for manufacturing connectionstructure according to the present embodiment is the same as the methodfor manufacturing connection structure according to the first embodimentexcept that the second composite 30′ is arranged on the second electrode114 and a region other than the second electrode 114 of the secondsurface. The same description as that of the first embodiment isomitted, and parts different from the methods for manufacturingconnection structure according to the first embodiment are describedherein.

The Method for Manufacturing Connection Structure

The method for manufacturing connection structure according to oneembodiment of the present invention is described by using FIG. 6A to 6F.Since the existing first electronic component 101 and second electroniccomponent 111 can be used in the present embodiment, their descriptionis omitted. In FIG. 6A to FIG. 6F, the method of forming the connectionstructure is described in detail.

First, the plurality of conductive particles 10 and the first composite20′ are arranged in a predetermined region on the first electrode 110.The plurality of conductive particles 10 and the first composite 20′ aremixed, and are arranged by using an offset printing scheme. Since themixture of the conductive particles 10 and the first composite 20′contains the conductive particles 10, a pad printing scheme oftransferring a printed matter by using a pad is particularly preferable.The region and method for arranging the mixture of the plurality ofconductive particles 10 and the first composite 20′ are the same asthose of the method for manufacturing connection structure according tothe first embodiment, and therefore are not described herein.

FIG. 6A and FIG. 6B show the process of transferring the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe pad 230 to the first electrode 110 by the pad printing scheme. Asshown in FIG. 6A and FIG. 6B, the pad 230 is pushed in a directionsubstantially perpendicular to the first electrode 110, and is thenpulled away in the direction substantially perpendicular to the firstelectrode 110, thereby transferring the mixture of the conductiveparticles 10 and the first composite 20′ displaced to the pad 230 ontothe first electrode 110. On the first surface of the first member 102,the conductive particles 10 and the first composite 20′ form a convexconfiguration in the opposing direction (D1 direction) of theelectrodes. The viscosity of the curable resin material of the firstcomposite 20′ is in the range between a value equal to or higher than5×10³ cP and a value equal to or lower than 5×10⁵ cP. Thus, theconductive particles 10 mixed into the first composite 20′ can beretained on the first electrode 110. The use of this method allows theconductive particles 10 and the first composite 20′ to be reliablyarranged in a predetermined region on the first electrode 110.

Next, the second composite 30′ is arranged on the second surface thesecond member 112. As shown in FIG. 6C and FIG. 6D, the second composite30′ is arranged in a region other than the second electrode 114 of thesecond surface of the second member 112. Furthermore, the secondcomposite 30′ is arranged also in a region on the second electrode 114other than the region where the plurality of conductive particles 10 andthe first composite 20′ are arranged, which will be described furtherbelow. The second composite 30′ is arranged also do the region on thesecond electrode 114 where the plurality of conductive particles 10 andthe first composite 20′ are arranged, which will be described furtherbelow. That is, the second composite 30′ is arranged on the secondelectrode 114 and a region other than the second electrode 114 of thesecond surface of the second member 112. In the present embodiment, thesecond composite 30′ is in a paste form, and is arranged by using aninkjet scheme or jet dispensing scheme. However, the method of arrangingthe second composite 30′ is not limited to this scheme, and any existingmethod can be used. For example, coating by inkjet or a dispenser,screen printing, or the like can be used.

The viscosity of the second composite 30′ is in a range between a valueequal to or higher than 2×10³ cP and a value equal to or lower than2×10⁵ cP. This allows a flow of the second composite 30′ to beinhibited.

Next, the second electronic component 111 is need on the first surfaceof the first electronic component 101. As shown in FIG. 6E, the firstsurface of the first member 102 and the second surface of the secondmember 112 are arranged so as to be opposed to each other so that thecorresponding plurality of first electrodes 110 and the plurality ofsecond electrodes 114 are opposed to each other. The first member 102and the second member 112 are pressed so that the first surface of thefirst member 102 and the second surface of the second member 112 arepushed in directions substantially perpendicular to the respectivesurfaces. The first surface of the first member 102 and the secondsurface of the second member 112 are pressure-welded to the conductiveparticles 10, the first composite 20′, and the second composite 30′.Here, the first composite 20′ arranged on the first electrode 110 has aviscosity higher than that of the second composite 30′, and is thusretained on the first electrode 110 together with the conductiveparticles 10. The second composite 30′ arranged on the second electrode114 has a viscosity lower than that of the first composite 20′, and thusmostly moves to a region other than the region where the conductiveparticles 10 and the first composite 20′ are arranged. That is, with astress being applied between the fast surface of the first member 102and the second surface of the second member 112, most of the secondcomposite 30′ positioned between the second electrode 114 and the firstcomposite 20′ moves, and the second composite 30′ positioned between thesecond electrode 114 and the conductive particles 10 eliminated.Furthermore, the composite 20′ and the conductive particles 10 formingthe convex configuration on the first surface of the first ember 102 areburied by the second composite 30′. In other words, most of the secondcomposite 30′ is arranged on the second surface of the second member 112in a region other than the region where the plurality of conductiveparticles 10 and the first composite 20′ are arranged (convexconfiguration). The conductive particles 10 arranged on the firstelectrode 110 are arranged so as to be in contact with the secondelectrode 114, and the second composite 30′ is arranged so as to be incontact with a region other than the first electrode 110 on the firstace and a region other than the second electrode 114 on the secondsurface, and the second electrode 114.

As shown in FIG. 6F, the first member 102 and the second member 112 arefurther pressed to push the first surface of the first member 102 andthe second surface of the second member 112 in the directionssubstantially perpendicular to the respective surfaces. Here, asufficient pressure is applied to cause the opposing first electrode 110and second electrode 114 to be in contact with upper and lower sides ofone conductive particle 10. The pressure to push the first surface ofthe first member 102 and the second surface of the second member 112 canbe adjusted a appropriate by a repulsive force of the conductiveparticles 10 and elastic forces of the first composite 20′ and thesecond composite 30′. This configuration allows electrical connectionbetween the first electrode 110 and the second electrode 114.

With the first member 102 and the second 12 pressed, the connectionstructure 100 is irradiated with light to cure the first composite 20′and the second composite 30′. A method of curing the first composite 20′and the second composite 30′ is the same as that of the method formanufacturing connection structure according to the first embodiment andis therefore not described herein. By curing the first composite 20′ andthe second composite 30′, the first resin 20 and the second resin 30 areformed. This configuration allows physical connection between the firstsurface of the first electronic component 101 and the second surface ofthe second electronic component 111.

According to the present embodiment, a connection structure and a methodfor manufacturing connection structure can be provided that can ensureconductivity between the opposing electrodes with a simple process andcan reduce short circuit between adjacent connection electrodes, even ifthe electrodes arranged on the electronic component have high finenessand high density. Furthermore, since no heat curing connection scheme isused the electrodes of the upper and lower substrates having differentcoefficients of thermal expansion can be connected with high accuracy.

Third Embodiment

The configuration of a connection structure according to a thirdembodiment is the same as the configuration of the connection structureaccording to the first embodiment except that the first resin 20 isarranged on the second electrode 114. A method for manufacturingconnection structure according to the present embodiment is the sane asthe method for manufacturing connection structure according to the firstembodiment except that the mixture of the plurality of conductiveparticles 10 and the first composite 20′ is arranged on the secondelectrode 114 and the second composite 30′ is arranged on the firstelectrode 110 and a region other than the first electrode 110 of thefirst surface. The same description as that of the first embodiment isomitted, and parts different from the connection structure and themethod for manufacturing connection structure according to the firstembodiment are described herein.

Configuration of Connection Structure

FIG. 7A to FIG. 7C show the configuration of the connection structureaccording to one embodiment of the present invention. FIG. 7A is a planview of the connection structure according to one embodiment of thepresent invention. FIG. 7B is a sectional view along a D-D′ line of FIG.7A. FIG. 7C is an enlarged sectional view of a conductive particle in aregion E of FIG. 7B.

As shown in FIG. 7A to FIG. 7C, the plurality of conductive particles 10are dispersed in the first resin 20 and the second resin 30 between thefirst electrode 110 and the second electrode 114. Each of the pluralityof conductive particles 10 are surrounded by the first resin 20 on thesecond electrode 114 in the surface direction (D2-D3 surface direction).Each of the plurality of conductive particles 10 are surrounded by thesecond resin 30 on the first electrode 110 the surface direction (D2-D3surface direction). The first resin 20 and the second resin 30 areinsulating resin. Thus a connection structure 100 a has insulationproperties in the surface direction (D2-D3 surface direction). However,the plurality of conductive particles 10 arranged between the opposingfirst electrode 110 and second electrode 114 and adjacent to each otherin the surface direction (D2-D3 surface direction) may be in contactwith each other. When the conductive particles 10 adjacent to each otherin the surface direction (D2-D3 surface direction) are in contact witheach other, the conductive particles 10 adjacent to each other are alsoelectrically connected. This arrangement allows the conductive particles10 to further reliably connect the opposing first electrode 110 andsecond electrode 114 electrically. The distance between the adjacentconductive particles 10 can be appropriately controlled according to theconcentration of the conductive particles 10 mixed into the firstcomposite 20′, which will be described further below.

The second resin 30 is further arranged between the first surface of thefirst member 102 and the second surface of the second member 112. Thesecond resin 30 is arranged in a region not between the opposing firstelectrode 110 and second electrode 114. The second resin 30 is arrangedbetween a region other the first electrode on the first surface and aregion other than the second electrode on the second surface. That is,the second resin 30 is arranged between the plurality of firstelectrodes 110 adjacent to each other in the surface direction (D2-D3surface direction) and on the periphery thereof (between the pluralityof second electrodes 114 adjacent to each other in the surface direction(D2-D3 surface direction) and on the periphery thereof). Furthermore,the second resin 30 is also arranged between the first electrode 110 andthe second electrode 114 in a region other than the region where theconductive particles 10 and the first resin 20 are arranged. The secondresin 30 is arranged between the regions adjacent in surface direction(D2-D3 surface direction) where the plurality of conductive particles 10and the first resin 20 are arranged and on the periphery thereof. Inother words, the conductive particles 10 and the first resin 20 aresurrounded by the second resin 30 in the surface direction (D2-D3surface direction). That is, when viewed in the opposing direction (D1direction) of the electrodes, the plurality of conductive particles 10are surrounded by the first resin 20, and the first resin 20 issurrounded by the second resin 30 on the second surface of the secondelectronic component 111. As shown in FIG. 7B and FIG. 7C, the secondresin 30 is further arranged between the first electrode 110 and thesecond electrode 114 in the region where the conductive particles 10 andthe first resin 20 are arranged. The second resin 30 is arranged betweenthe first resin 20 and the first electrode 110. That is, when viewed inthe opposing direction (D1 direction) of the electrodes, the pluralityof conductive particles 10 are surrounded by the second resin 30 on thefirst surface of the first electronic component 101. The first resin 20and the second resin 30 are insulating resin. Thus, the connectionstructure 100 a has insulation properties in the surface direction(D2-D3 surface direction). This arrangement allows the second resin 30to reliably insulate between the plurality of first electrodes 110adjacent in the surface direction (D2-D3 surface direction), between theplurality of second electrodes 114 adjacent in the surface direction(D2-D3 surface direction), and between the first electrode 110 and thesecond electrode 114 not opposed to each other.

The first resin 20 and the second resin 30 are arranged between thefirst electrode 110 and the second electrode 114 so that the first resin20 is in contact with the second electrode 114 and the second resin 30is in contact with the first electrode 110. That is, the first resin 20and the second resin 30 are in contact in the surface direction (D2-D3surface direction) between the first electrode 110 and the secondelectrode 114 and are laminated in the opposing direction (D1 direction)of the electrodes.

The Method for Manufacturing Connection Structure

The method for manufacturing connection structure according to oneembodiment of the present invention is described by using FIG. 8A to 8F.Since the existing first electronic component 101 and second electroniccomponent 111 can be used in the present embodiment, their descriptionis omitted. In FIG. 8A to FIG. 8F, the method of forming the connectionstructure 100 a is described in detail.

First, the plurality of conductive particles 10 and the first composite20′ are arranged in a predetermined region on the second electrode 114.The plurality of conductive particles 10 and the first composite 20′ aremixed, and are arranged by using an offset printing scheme. Since themixture of the conductive particles 10 and the first composite 20′contains the conductive particles 10, a pad printing scheme oftransferring a printed matter by using a pad is particularly preferable.The region and method for arranging the mixture of the plurality ofconductive particles 10 and the first composite 20′ are the same asthose of the method for manufacturing connection structure according tothe first embodiment, and therefore are not described herein.

FIG. 8A and FIG. 8B show a process of transferring the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe pad 230 to the second electrode 114 by the pad printing scheme. Asshown in FIG. 8A and FIG. 8B, the pad 230 is pushed in a directionsubstantially perpendicular to the second electrode 114, and is thenpulled away in the direction substantially perpendicular to the secondelectrode 114, thereby transferring the mixture of the conductiveparticles 10 and the first composite 20′ displaced to the pad 230 ontothe second electrode 114. On the second surface of the second member112, the conductive particles 10 and the first composite 20′ form aconvex configuration in the opposing direction (D1 direction) of theelectrodes. The viscosity of the curable resin material of the firstcomposite 20′ is in the range between a value equal to or higher than5×10³ cP and a value equal to or lower than 5×10⁵ cP. Thus, theconductive particles 10 mixed into the first composite 20′ can beretained on the second electrode 114. The use of this method allows theconductive particles 10 and the first composite 20′ to be reliablyarranged in a predetermined region on the second electrode 114.

Next, the second composite 30′ is arranged on the first surface of thefirst member 102. As shown in FIG. 8C and FIG. 8D, the second composite30′ is arranged in a region other than the first electrode 110 of thefirst surface of the first member 102. Furthermore, the second composite30′ is arranged also in a region on the first electrode 110 other thanthe region where the plurality of conductive particles 10 and the firstcomposite 20′ are arranged which will be described further below. Thesecond composite 30′ is arranged also on the region on the firstelectrode 110 where the plurality of conductive particles 10 and thefirst composite 20′ are arranged, which will be described further below.That is, the second composite 30′ is arranged on the first electrode 110and a region other than the first electrode 110 of the first surface ofthe first member 102. In the present embodiment, the second composite30′ is in a paste form, and is arranged by using an inkjet scheme or jetdispensing scheme. However, the method of arranging the second composite30′ is not limited to this scheme, and any existing method can be used.For example, coating by inkjet or a dispenser, screen printing, or thelike can be used.

The viscosity of the second composite 30′ is in a range between a valueequal to or higher than 2×10³ cP and a value equal to or lower than2×10⁵ cP. This allows a flow of the second composite 30′ to beinhibited.

Next, the second electronic component 111 is mounted on the firstsurface of the first electronic component 101. As shown in FIG. 8E, thefirst surface of the first member 102 and the second surface of thesecond member 112 are arranged so as to be opposed to each other so thatthe corresponding plurality of first electrodes 110 and the plurality ofsecond electrodes 114 are opposed to each other. The first member 102and the second member 112 are pressed so that the first surface of thefirst member 102 and the second surface of the second member 112 arepushed in directions substantially perpendicular to the respectivesurfaces. The first surface of the first member 102 and the secondsurface of the second member 112 are pressure-welded to the conductiveparticles 10, the first composite 20′, and the second composite 30′.Here, the first composite 20′ arranged on the second electrode 114 has aviscosity higher than that of the second composite 30′, and is thusretained on the second electrode 114 together with the conductiveparticles 10. The second composite 30′ arranged on the first electrode110 has a viscosity lower than that of the first composite 20′, and thusmostly moves to a region other than the region where the conductiveparticles 10 and the first composite 20′ are arranged. That is, with astress being applied between the first surface of the first member 102and the second surface of the second member 112, most of the secondcomposite 30′ positioned between the first electrode 110 and the firstcomposite 20′ moves, and the second composite 30′ positioned between thefirst electrode 110 and the conductive particles 10 is eliminated.Furthermore the first composite 20′ and the conductive particles 10forming the convex configuration on the second surface of the secondmember 112 are buried by the second composite 30′. In other words, mostof the second composite 30′ is arranged on the first surface of thefirst member 102 in a region other than the region where the pluralityof conductive particles 10 and the first composite 20′ are arranged(convex configuration). The conductive particles 10 arranged on thesecond electrode 114 are arranged so as to be in contact with the firstelectrode 110, and the second composite 30′ so as to be in contact witha region other than the first electrode 110 on the first surface and aregion other than the second electrode 114 on the second surface, andthe first electrode 110.

As shown in FIG. 8F, the first member 102 and the second member 112 arefurther pressed to push the first surface of the first member 102 andthe second surface of the second member 112 in the directionssubstantially perpendicular to the respective surfaces. Here, asufficient pressure is applied to cause the opposing first electrode 110and second electrode 114 to be in contact with upper and lower sides ofone conductive particle 10. The pressure to push the first surface ofthe first member 102 and the second surface of the second member 112 canbe adjusted as appropriate by a repulsive force of the conductiveparticles 10 and elastic forces of the first composite 20′ and thesecond composite 30′. This configuration allows electrical connectionbetween the first electrode 110 and the second electrode 114.

With the first member 102 and the second member 112 pressed, theconnection structure 100 a is irradiated with light to cure the firstcomposite 20′ and the second composite 30′. A method of curing the firstcomposite 20′ and the second composite 30′ is the same as that of themethod for manufacturing connection structure according to theembodiment, and is therefore not described herein. By curing the firstcomposite 20′ and the second composite 30′, the first resin 20 and thesecond resin 30 are formed. This configuration allows physicalconnection between the first surface of the first electronic component101 and the second surface of the second electronic component 111.

According to, the present embodiment, a connection structure and amethod for manufacturing connection structure can be provided that canensure conductivity between the opposing electrodes with a simpleprocess and can reduce a short circuit between adjacent connectionelectrodes, even if the electrodes arranged on the electronic componenthave high fineness and high density. Furthermore since no heat curingconnection scheme is used, the electrodes of the upper and lowersubstrates having different coefficients of thermal expansion can beconnected with high accuracy.

Fourth Embodiment

The configuration of a connection structure according to a fourthembodiment is the same as the configuration of the connection structureaccording to the third embodiment. A method for manufacturing connectionstructure according to the present embodiment is the same as the methodfor manufacturing connection structure according to the third embodimentexcept that the second composite 30′ is arranged on the second electrode114 and a region other than the second electrode 114 of the secondsurface. The same description as that of the first embodiment and thethird embodiment is omitted, and parts different from the method formanufacturing connection structure according to the first embodiment andthe third embodiment are described herein.

The Method for Manufacturing Connection Structure

The method for manufacturing connection structure according to oneembodiment of the present invention is described by using FIG. 9A toFIG. 9E. Since the existing first electronic component 101 and secondelectronic component 111 can be used in the present embodiment, theirdescription is omitted. In FIG. 9A to FIG. 9E, the method of forming theconnection structure 100 a is described in detail.

First, the plurality of conductive particles 10 and the first composite20′ are arranged in a predetermined region on the second electrode 114.The plurality of conductive particles 10 and the first composite 20′ aremixed, and are arranged by using an offset printing scheme. Since themixture of the conductive particles 10 and the first composite 20′contains the conductive particles 10, a pad printing scheme oftransferring a printed matter by using a pad is particularly preferable.The region and method for arranging the mixture of the plurality ofconductive particles 10 and the first composite 20′ are the same asthose of the method for manufacturing connection structure according tothe first embodiment, and therefore are not described herein.

FIG. 9A and FIG. 9B show a process of transferring the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe pad 230 to the second electrode 114 by the pad printing scheme. Asshown in FIG. 9A and FIG. 9B, the pad 230 is pushed in a directionsubstantially perpendicular to the second electrode 114, and is thenpulled away in the direction substantially perpendicular to the secondelectrode 114, thereby transferring the mixture of the conductiveparticles 10 and the first composite 20′ displaced to the pad 230 ontothe second electrode 114. On the second surface of the second member112, the conductive particles 10 and the first composite 20′ form convexconfiguration in the opposing direction (D1 direction) of theelectrodes. The viscosity of the curable resin material of the firstcomposite 20′ is in the range between a value equal to or higher than5×10³ cP and a value equal to or lower than 5×10⁵ cP. Thus, theconductive particles 10 mixed into the first composite 20′ can beretained on the second electrode 114. The use of this method allows theconductive particles 10 and the first composite 20′ to be reliablyarranged in a predetermined region on the second electrode 114.

Next the second composite 30′ is arranged on the second surface of thesecond member 112. As shown in FIG. 9C and FIG. 9D, the second composite30′ is arranged in a region other than the second electrode 114 of thesecond surface of the second member 112. Furthermore, the secondcomposite 30′ arranged also in a region on the second electrode 114other than the region ere the plurality of conductive particles 10 andthe first composite 20′ are arranged, which will be described furtherbelow. Still further, the second composite 30′ is arranged also on theregion on the second electrode 114 where the plurality of conductiveparticles 10 and the first composite 20′ are arranged. That is, thesecond composite 30′ is arranged on the second electrode 114 and theregion other than the second electrode 114 of second surface of thesecond member 112. In the present embodiment, the second composite 30′is in paste form, and is arranged by using an inkjet scheme or jetdispensing scheme. However, the method of arranging the second composite30′ is not limited to this scheme, and any existing method can be used.For example, coating by inkjet or a dispenser, screen printing, or thelike can be used.

The viscosity of the second composite 30′ is in a range between a valueequal to or higher than 2×10³ cP and a value equal to or lower 2×10⁵ cP.This allows a flow of the second composite 30′ to be inhibited.

Next, the second electronic component 111 is mounted on the firstsurface of the first electronic component 101. As shown in FIG. 9E, thefirst surface of the first member 102 and the second surface of thesecond member 112 are arranged so as to be opposed to each other so thatthe corresponding plurality of first electrodes 110 and the plurality ofsecond electrodes 114 are opposed to each other. The first member 102and the second member 112 are pressed so that the first surface of thefirst member 102 and the second surface of the second member 112 arepushed in directions substantially perpendicular to the respectivesurfaces. The first surface of the first member 102 and the secondsurface of the second member 112 are pressure-welded to the conductiveparticles 10, the first composite 20′, and the second composite 30′.Here, the first composite 20′ arranged on the second electrode 114 has aviscosity higher than that of the second composite 30′, and is thusretained on the second electrode 114 together with the conductiveparticles 10. The second composite 30′ arranged on the second electrode114 has a viscosity lower than that of the first composite 20′, and thusmostly moves to a region other than the region where the conductiveparticles 10 and the first composite 20′ are arranged. That is, with astress being applied between the first surface the first member 102 andthe second surface of the second member 112, most of the secondcomposite 30′ positioned between the first electrode 110 and the firstcomposite 20′ moves, and the second composite 30′ positioned between thefirst electrode 110 and the conductive particles 10 is eliminated.Furthermore, the first composite 20′ and the conductive particles 10forming the convex configuration on the second surface of the secondmember 112 are buried by the second composite 30′. In other words, mostof the second composite 30′ is arranged on the second surface of thesecond member 112 in a region other than the region where the pluralityof conductive particles 10 and the first composite 20′ are arranged(convex configuration). The conductive particles 10 arranged on thesecond electrode 114 are arranged so as to be in contact with theelectrode 110, and the second composite 30′ is arranged so as to be incontact with a region other than the first electrode 110 on the firstsurface and a region other than the second electrode 114 on the secondsurface, and the first electrode 110.

As shown in FIG. 9F, the first member 102 and the second member 112 arefurther pressed to push the first surface of the first member 102 andthe second surface of the second member 112 in the directionssubstantially perpendicular to the respective surfaces. Here, asufficient pressure is applied to cause the opposing first electrode 110and second electrode 114 to be in contact with upper and lower sides ofone conductive particle 10. The pressure to push the first surface ofthe first member 102 and the second surface of the second member 112 canbe adjusted as appropriate by a repulsive force of the conductiveparticles 10 and elastic forces of the first composite 20′ and thesecond composite 30′. This configuration allows electrical connectionbetween the first electrode 110 and the second electrode 114.

With the first member 102 and the second member 112 pressed, theconnection structure 100 a is irradiated with light to cure the firstcomposite 20′ and the second composite 30′. A method of curing the firstcomposite 20′ and the second composite 30′ is the same as that of themethod for manufacturing connection structure according to the firstembodiment, and is therefore not described herein. By curing the firstcomposite 20′ and the second composite 30′, the first resin 20 and thesecond resin 30 are formed. This configuration allows physicalconnection between the first surface of the first electronic component101 and the second surface of the second electronic component 111.

According to the present embodiment, a connection structure and a methodfor manufacturing connection structure can be provided that can ensureconductivity between the opposing electrodes with a simple process andcan reduce a short circuit between adjacent connection electrodes, evenif the electrodes arranged on the electronic component have highfineness and high density. Furthermore, since no heat curing connectionscheme is used, the electrodes of the upper and lower substrates havingdifferent coefficients of thermal expansion can be connected with highaccuracy.

Fifth Embodiment

The configuration of the connection structure according to a fifthembodiment is the same as the configuration of the connection structureaccording to the first embodiment except that the first resin 20 isarranged also in a region other than the first electrode of the firstmember 102. A method for manufacturing connection structure according tothe present embodiment is the same as the method for manufacturingconnection structure according to the first embodiment except that thefirst composite 20′ is also arranged in a region other than the firstelectrode 110 of the first surface. The same description as that of thefirst embodiment is omitted, and parts different from the connectionstructure and the method for manufacturing connection structureaccording to the first embodiment are described herein.

Configuration of Connection Structure

FIG. 10A to FIG. 10C show the configuration of the connection structureaccording to one embodiment of the present invention. FIG. 10A is a planview of the connection structure according to one embodiment of thepresent invention. FIG. 10B is a sectional view along a F-F′ line ofFIG. 10A FIG. 10C is an enlarged sectional view of a conductive particlein a region G of FIG. 10B.

As shown in FIG. 10A and FIG. 10B, a connection structure 100 b includesthe first member 102 having the first surface, the first electrode 110the second member 112 having the second surface, the second electrode114, the conductive particles 10, the first resin 20, and the secondresin 30. A plurality of first electrodes 110 and a plurality of secondelectrode 114 are arranged so as to be the first electrode 110 and thesecond electrode 114 are opposed to each other. The plurality ofconductive particles 10, the first resin 20, and the second resin 30 arearranged between the opposing electrode 110 and second electrode 111.The plurality of conductive particles 10 are arranged in the surfacedirection (D2-D3 surface direction) between the opposing first electrode110 and second electrode 114. One conductive particle 10 is arrangedbetween the opposing first electrode 110 and second electrode 114 in theopposing direction (D1 direction) of the first electrode 110 and thesecond electrode 114. Each of the plurality of conductive particles 10are in contact with the opposing first electrode 110 and secondelectrode 114. As shown in FIG. 10C, the conductive particle 10 ispressured and deformed in the opposing direction (D1 direction) betweenthe first electrode 110 and the second electrode 114 by a method formanufacturing connection structures which will be described furtherbelow. That is, a distance between the first electrode 110 and thesecond electrode 114 in the opposing direction (D1 direction) of theelectrodes is substantially equal to the height of the conductiveparticle 10 in the opposing direction (D1 direction) of the electrodes.The height of the conductive particle 10 in the opposing direction (D1direction) of the electrodes is pressured and deformed by approximately10% to 40%. With a stress provided among the first electrode 110, theconductive particles 10, and the second electrode 114, the first resin20 and the second resin 30 are eliminated at the contact part betweenthe first electrode 110 and the conductive particle 10 and the contactpart between the second electrode 114 and the conductive particle 10.Furthermore, even natural oxide film is formed on the first electrode110, the conductive particle 10, or the second electrode 114 and itssurface is insulated, the first electrode 110 and the second electrode114 are pressure-welded with the conductive particle 10 interposedtherebetween thereby breaking the natural oxide film to form aconductive route. Furthermore, deformation of the conductive particle 10can increase the area of contact between the first electrode 110 and theconductive particle 10 and the area of contact between the secondelectrode 114 and the conductive particle 10. This arrangement allowsthe conductive particle 10 to electrically connect the first electrode110 and the second electrode 114.

As in FIG. 10A and FIG. 10B, the plurality of conductive particles 10,the first resin 20, and the second resin 30 are arranged between thefirst electrode 110 and the second electrode 114. In the presentembodiment, the plurality of conductive particles 10, the first resin20, and the second resin 30 are arranged on a substantially entire uppersurface of the first electrode 110 when viewed in the opposing direction(D1 direction) of the electrodes. The diameter of the conductiveparticle 10 when viewed in the opposing direction (D1 direction) of theelectrodes is in a range between a value equal to or larger than 2 μmand a value equal to or smaller than 10 μm. The number of conductiveparticles 10 arranged between the opposing first electrode 110 andsecond electrode 114 when viewed in the opposing direction (D1direction) of the electrodes is preferably in a range between a valueequal to or larger then seven per 400 μm² and a value equal to orsmaller than twenty per 400 μm². This arrangement allows the conductiveparticles 10 to reliably connect the opposing first electrode 110 andsecond electrode 114 and can prevent a short circuit between theplurality of first electrodes 110 adjacent to each other in the surfacedirection (D2-D3 surface direction), between the plurality of secondelectrodes 114 adjacent to each other in the surface direction (D2-D3surface direction), and between the first electrode 110 and the secondelectrode 114 not opposed to each other.

In the present embodiment, the shape of the region where the conductiveparticles 10 and the first resin 20 are arranged when viewed in theopposing direction (D1 direction) of the electrodes is a rectangle so asto match the first electrode 110. However, the shape is not limited tothis, and the region where the conductive particles 10 and the firstresin 20 are arranged may have any shape having an area within theabove-described range.

The area of the region arranged on the upper surface of one firstelectrode 110 where the conductive particles 10 and the first resin 20are arranged can be adjusted as appropriate to satisfy theabove-described condition, depending on the area of the first electrode110, the size of the conductive particles 10, and so forth. The numberof conductive particles 10 arranged in the region where the conductiveparticles 10 and the first resin 20 are arranged can be adjusted asappropriate to satisfy the above-described condition, depending on thesize of the conductive particles 10 and the concentration of theconductive particles 10 mixed into the first composite 20′, which willbe described further below.

In the present embodiment, the first resin 20 is arranged also in aregion other than the first electrode 110 of the first surface whenviewed in the opposing direction (D1 direction) of the electrodes. Thefirst resin 20 is arranged also between the plurality of firstelectrodes 110 and around the plurality of first electrodes 110 on thefirst surface when viewed in the opposing direction (D1 direction) ofthe electrodes. On the other hand, the first resin 20 is not arranged atan end of the first surface when viewed in the opposing direction (D1direction) of the electrodes. Here, the conductive particles 10 are notarranged in a region other than the first electrode 110 of the firstsurface (the second electrode 114 of the second surface) when viewed inthe opposing direction (D1 direction) of the electrodes. That is, theconductive particles 10 are arranged on the first electrode 110 (or thesecond electrode 114).

The second resin 30 is further arranged between the first surface of thefirst member 102 and the second surface of the second member 112. Thesecond resin 30 is arranged in a region not between the opposing firstelectrode 110 and second electrode 114. In the present embodiment, thesecond resin 30 is arranged in a region other than the second electrode114 of the second surface when viewed in the opposing direction (D1direction) of the electrodes. That is, the second resin 30 is arrangedon the second surface of the second member 112 between the plurality ofsecond electrodes 114 adjacent to each other in the surface direction(D2-D3 surface direction) and on the periphery thereof. The second resin30 is arranged also at ends of the first surface and the second surfacewhen viewed in the opposing direction (D1 direction) of the electrodes.As shown in FIG. 10B and FIG. 10C, the second resin 30 is furtherarranged also between the first electrode 110 and the second electrode114 in the region where the conductive particles 10 and the first resin20 are arranged. The second resin 30 is arranged between the first resin20 and the second electrode 114. That is, when viewed in the opposingdirection (D1 direction) of the electrodes, the conductive particles 10arranged on the second electrode 114 on the second surface of the secondmember 112 are surrounded by the second resin 30 in the surfacedirection (D2-D3 surface direction). The first resin 20 and the secondresin 30 are insulating resin. Thus, the connection structure 100 b hasinsulation properties in the surface direction (D2-D3 surfacedirection). This arrangement allows the second resin 30 to reliablyinsulate between the plurality of first electrodes 110 adjacent in thesurface direction (D2-D3 surface direction), between the plurality ofsecond electrodes 114 adjacent in the surface direction (D2-D3 surfacedirection), and between the first electrode 110 and the second electrode114 not opposed to each other.

The first resin 20 and the second resin 30 are arranged between theregion other than the first electrode 110 of the first surface and theregion other than the second electrode 114 of the second surface. Thefirst resin 20 and the second resin 30 are arranged between theplurality of first electrodes 110 adjacent to each other in the surfacedirection (D2-D3 surface direction) and on the periphery thereof andbetween the plurality of second electrodes 114 adjacent to each other inthe surface direction (D2-D3 surface direction) and on the peripherythereof. Furthermore, the first resin 20 and the second resin 30 arearranged also between the first electrode 110 and the second electrode114. The first resin 20 is arranged so as to be in contact with thefirst surface, and the second resin 30 is arranged so as to be incontact with the second surface. That is, the first resin 20 and thesecond resin 30 are in contact in the surface direction (D2-D3 surfacedirection) between the first surface of the first electronic component101 and the second surface of the second electronic component 111 andare laminated in the opposing direction (D1 direction) of theelectrodes. On the other hand, the second resin 30 is arranged at theends of the first surface and the second surface when viewed in theopposing direction (D1 direction) of the electrodes.

The Method for Manufacturing Connection Structure

The method for manufacturing connection structure according to oneembodiment of the present invention is described by using FIG. 11A toFIG. 14E. Since the existing first electronic component 101 and secondelectronic component 111 can be used in the present embodiment, theirdescription is omitted. In FIG. 11A to FIG. 14E, the method of formingthe connection structure 100 b is described in detail.

First, the first composite 20 is arranged on the first surface of thefirst member 102, and the plurality of conductive particles 10 arearranged on the upper surface of the first electrode 110. The pluralityof conductive particles 10 and the first composite 20′ are mixed, andare arranged by using an offset printing scheme. Since the mixture ofthe conductive particles 10 and the first composite 20′ contains theconductive particles 10, a pad printing scheme of transferring a printedmatter by using a pad is particularly preferable. By using FIG. 11A toFIG. 14E, a method of arranging the plurality of conductive particles 10and the first composite 20′ is described.

FIG. 11A to FIG. 11C show a process of arranging the mixture of theplurality of conductive particles 10 and the first composite 20′ on aplate 240. FIG. 12A to FIG. 12C are sectional views along a H-H′ line ofFIG. 11A to FIG. 11C. In the present embodiment, the plate 240 is, forexample, a planographic intaglio plate. In the present embodiment, theplate 240 has depressed parts 246 corresponding to the first electrodes110. However, the depressed parts 246 are not limited to correspond tothe first electrodes 110, and are only required to correspond to regionson the first surface of the first member 102 where the plurality ofconductive particles 10 and the first composite 20′ are arranged.

In the present embodiment, the mixture of the conductive particles 10and the first composite 20′ is arranged on the plate 240 by using blade250. However, the mixture of the conductive particles 10 and the firstcomposite 20′ is not limited to be arranged by using the blade, but maybe arranged on the plate 240 by using a roller or the like. As shown inFIG. 11A to FIG. 11C and FIG. 12A to FIG. 12C, the blade 250 is movedfrom one end to the other end of the plate 240 with its tip beingseparated from an upper surface 244 of the plate 240. A gap between thetip of the blade 250 and the upper surface 244 of the plate 240 can beset as appropriate in a range between a value larger than 0 μm and avalue smaller than Y μm, with the diameter of the conductive particle 10being taken as Y μm. Since the gap distance is smaller than the diameterof the conductive particle 10 of Y μm, the conductive particles 10 arenot arranged but the first composite 20′ is arranged on the uppersurface 244 of the plate 240.

The depth from the tip of the blade 250 to a bottom surface 242 of thedepressed part 246 can be selected as appropriate in a range larger thanY μm when the diameter of the conductive particle 10 is taken as Y.Since the depth from the tip of the blade 250 to the bottom surface 242of the depressed part 246 is larger than the diameter Y μm of theconductive particle 10, the conductive particles 10 are arranged in thedepressed parts 246 together with the first composite 20′.

If the distance from the tip of the blade 250 to the bottom surface 242of the depressed part 246 is smaller than Y μm, the tip of the blade 250and the conductive particles 10 tend to make contact, and the conductiveparticles 10 may not be filled or the filled conductive particles 10 maybe damaged. If the gap distance between the tip of the blade 250 and theupper surface 244 of the plate 240 is larger than Y μm, there is apossibility of arranging the conductive particles 10 on the uppersurface 244 of the plate 240.

As shown in FIG. 11A to FIG. 11C and FIG. 12A to FIG. 12C, with theblade 250 being moved from one end to the other end of the plate 240,the conductive particles 10 and the first composite 20′ are arranged onthe plate 240. In the present embodiment, the blade 250 is preferablymoved from one end to the other end of the plate 240 in a short sidedirection (D3 direction) of the depressed parts 246. This allowsimbalance of the conductive particles 10 arranged in one depressed part246 to be inhibited.

As for the concentration of the conductive particles 10 mixed into thefirst composite 20′, the ratio of the conductive particles 10 to thetotal volume of the conductive particles 10 and the first composite 20′is preferably in a range between a value equal to or larger than 20volume % and a value equal to or smaller than 60 volume %. If the mixingamount of the conductive particles 10 is smaller than 20 volume %, it isdifficult to fill the sufficient number of conductive particles 10 inthe depressed parts 246. If the mixing amount of the conductiveparticles 10 is larger than 60 volume %, operability is degraded, and itis difficult to fill the mixture of the conductive particles 10 and thefirst composite 20′ in the depressed parts 246. By arranging the mixtureof the conductive particles 10 and the first composite 20′ with theblade 250, the conductive particles 10 and the first composite 20′ canbe filled in the depressed parts 246 of the plate 240, and the firstcomposite 20′ is arranged on the upper surface 244 of the plate 240.

Since the depressed parts 246 have the depth in the above-describedrange, one conductive particle 10 can be retained in the depth direction(D1 direction) of the depressed parts 246. The number of conductiveparticles 10 arranged in one depressed part 246 when viewed from theupper surface of the plate 240 is preferably in a range between a valueequal to or larger than seven per 400 μm² and a value equal to orsmaller than twenty per 400 μm². This arrangement allows the conductiveparticles 10 and the first composite 20′ to be efficiently displaced tothe pad in a process of displacing the mixture of the conductiveparticles 10 and the first composite 20′ to the pad, which will bedescribed further below.

The depressed parts 246 are preferably separated each other by 5 μm ormore. If the depressed parts 246 are separated from each other by lessthan 5 μm, walls separating the adjacent depressed parts 246 tend to bedamaged, and durability of the plate 240 may be degraded.

In the present embodiment, the shape of each depressed part 246 whenviewed in the opposing direction (D1 direction) of the electrodes is arectangle, which is the same as the first electrode 110 (or the secondelectrode 114). Also, the depressed part 246 has a same shape in a depthdirection. That is, the depressed part 246 has a shape obtained bycutting out a cuboid from the plate 240. However, the shape of thedepressed part 246 is not limited to this, and the depressed part 246can take any shape with the depth and the area in the above-describedrange. For example, the depressed part 246 can take a complex shape.

The plate 240 may be, for example, a glass intaglio plate, a nickelintaglio plate, or a stainless intaglio plate. As required, the plate240 may be subjected to plasma surface treatment using fluorine-basedgas, nickel plating, or DLC (Diamond Like Carbon) process to improvedurability of the plate 240.

FIG. 13A to FIG. 13C show a process of displacing the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe plate 240 to the pad 230. As shown in FIG. 13A to FIG. 13C, the pad230 is pressed in a direction substantially perpendicular to the plate240, and is then pulled away in the direction substantiallyperpendicular to the plate 240, thereby displacing, to the pad 230, thefirst composite 20′ arranged on the upper surface 244 of the plate 240and the conductive panicles 10 and the first composite 20′ filled in thedepressed parts 246 of the plate 240. Since the viscosity of the firstcomposite 20′ is in a range between a value equal to or higher than5×10³ cP and a value equal to or lower than 5×10⁵ cP, the conductiveparticles 10 mixed into the first composite 20′ can be retained on thesurface of the pad 230.

FIG. 14A and FIG. 14B show a process of transferring the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe pad 230 to the first surface of the first member 102. As shown inFIG. 14A and FIG. 14B, the pad 230 is pressed in a directionsubstantially perpendicular to the first surface and is then pulled awayin the direction substantially perpendicular to the first surface,thereby transferring the mixture of the conductive particles 10 and thefirst composite 20 displaced to the pad 230 onto the first surface.Here, the first composite 20′ and the conductive particles 10 to betransferred from the depressed parts 246 of the plate 240 are arrangedso as be in contact with the first electrode 110. That is, the firstcomposite 20′ is arranged on the first surface of the first member 102,and the conductive particles 10 are arranged on the upper surface of thefirst electrode 110. The viscosity of the curable resin material of thefirst composite 20′ is in the range between a value equal to or higherthan 5×10³ cP and a value equal to or lower than 5×10⁵ cP. Thus, theconductive particles 10 mixed into the first composite 20″ can beretained on the first electrode 110. The use of this method allows theconductive particles 10 and the first composite 20′ to be reliablyarranged in a predetermined region on the first electrode 110.

With the depth of the depressed parts 246, the first composite 40′ andthe conductive particles 10 transferred from the depressed parts 246 ofthe plate 240 are thickly arranged in the opposing direction (D1direction) of the electrodes on the first electrode 110 on the firstmember 102. On the other hand, without the depth of the depressed parts246, the first composite 20′ transferred from the upper surface 244 ofthe plate 240 is thinly arranged in the opposing direction (D1direction) of the electrodes in the region other than the firstelectrode 110 on the first member 102. However, this is not meant to berestrictive, and the first composite 20′ may not be transferred from theupper surface 244 of the plate 240 to the pad 230. On the first surfaceof the first member 102, the first composite 20′ forms a convex/concaveconfiguration in the opposing direction (D1 direction) of theelectrodes. On the first surface of the first member 102, the conductiveparticles 10 form a convex configuration together with the firstcomposite 20′. In the present embodiment, the plate 240 is smaller thanthe first surface (connection surface) of the first member 102. Thus,the first composite 20′ is not arranged at the end of the first surface.

Next, the second composite 30′ is arranged on the first surface of thefirst member 102. As shown in FIG. 14C, the second composite 30′ isarranged in a region other than the first electrode 110 of the firstsurface. Furthermore, the second composite 30′ is arranged also n thefirst electrode 110 of the first surface. Here, the first composite 20′transferred from the upper surface 244 of the plate 240 is arranged inthe region other than the first electrode 110 of the first surface.Also, the conductive particles 10 and the first composite 20′transferred from the depressed parts 246 of the plate 240 are arrangedon the first electrode 110 of the first surface. Thus, the secondcomposite 30′ is arranged to be superposed so as to be in contact withthe conductive particles 10 and the first composite 20′. The secondcomposite 30′ is arranged also at the end of the first surface. In thepresent embodiment, the second composite 30′ is in a paste form, and isarranged by using an inkjet scheme or jet dispensing scheme. However,the method of arranging the second composite 30 is not limited to thisscheme, and any existing method can be used. For example, coating byinkjet or a dispenser, screen printing, or the like can be used.

The viscosity of the second composite 30′ is in a range between a valueequal to or higher than 2×10³ cP and a value equal to or lower than2×10⁵ cP. It is required that the viscosity of the first composite 20′is twice as high as high as the viscosity of the second composite 30′ orhigher. This allows a flow of the conductive particles 10 mixed into thefirst composite 20′ to be inhibited and the conductive particles 10 canbe retained on the first electronic component 101.

Next, the second member 112 is mounted on the first surface of the firstmember 102. As shown in FIG. 14D, the first surface of the first member102 and the second surface of the second member 112 are arranged so asto be opposed to each other so that the corresponding plurality of firstelectrodes 110 and the plurality of second electrodes 114 are opposed toeach other. The first member 102 and the second member 112 are pressedso that the first surface of the first member 102 and the second surfaceof the second member 112 are pushed in directions substantiallyperpendicular to the respective. The first surface of the first member102 and the second surface of the second member 112 are pressure-weldedto the conductive particles 10, the first composite 20′, and the secondcomposite 30′. Here, the first composite 20′ arranged on the firstelectrode 110 has a viscosity higher than that of the second composite30′, and is thus retained on the first electrode 110 together with theconductive particles 10. The second composite 30′ arranged on the firstelectrode 110 has a viscosity lower than that of the first composite 20′and thus mostly moves to a region other than the region where theconductive particles 10 and the first composite 20′ are arranged. Thatis, with a stress being applied between the first surface of the firstmember 102 and the second surface of the second member 112, most of thesecond composite 30′ positioned between the second electrode 114 and thefirst composite 20′ moves, and the second composite 30′ positionedbetween the second electrode 114 and the conductive particles 10 iseliminated. Furthermore, the first composite 20′ and the conductiveparticles 10 forming the convex/concave configuration on the firstsurface of the first member 102 are buried by the second composite 30′.In other words, most of the second composite is arranged on the secondsurface of the second member 112 in a region other than the region wherethe plurality of conductive particles 10 and the first composite 20′ arearranged (convex configuration). The second composite 30′ is arranged onthe first surface of the first member 102 and a region where the firstcomposite 20′ is arranged (concave configuration). The conductiveparticles 10 arranged on the first electrode 110 are arranged so as tobe in contact with the second electrode 114, and the second composite30′ is arranged so as to be in contact with the first composite 20′arranged in a region other than the first electrode 110 on the firstsurface, a region other than the second electrode 114 on the secondsurface, and the second electrode 114.

As shown in FIG. 14E, the first member 102 and the second member 112 arefurther pressed to push the first surface of the first member 102 andthe second surface of the second member 112 in the directionssubstantially perpendicular to the respective surfaces. Here, asufficient pressure is applied to cause the opposing first electrode 110and second electrode 114 to be in contact with upper and lower sides ofone conductive particle 10. The pressure to push the first surface ofthe first member 102 and the second surface of the second member 112 canbe adjusted as appropriate by a repulsive force of the conductiveparticles 10 and elastic forces of the first composite 20′ and thesecond composite 30′.

With the first member 102 and the second member 112 pressed, theconnection structure 100 b is irradiated with light to cure the firstcomposite 20′ and the second composite 30′. A method of curing the firstcomposite 20′ and the second composite 30′ is the same as that of themethod for manufacturing connection structure according to the firstembodiment, and is therefore not described herein. By curing firstcomposite 20′ and the second composite 30′, the first resin 20 and thesecond resin 30 are formed. This configuration allows physicalconnection between the first surface of the first electronic component101 and the second surface of the second electronic component 111.

According to the present embodiment, a connection structure and a methodfor manufacturing connection structure can be provided that can ensureconductivity between the opposing electrodes with a simple process andcan reduce a short circuit between adjacent connection electrodes, evenif the electrodes arranged on the electronic component have highfineness and high density. Furthermore, since no heat curing connectionscheme is used, the electrodes of the upper and lower substrates havingdifferent coefficients of thermal expansion can be connected with highaccuracy.

Sixth Embodiment

The configuration of a connection structure according to a sixthembodiment is the same as the configuration of the connection structureaccording to the fifth embodiment. A method for manufacturing connectionstructure according to the present embodiment is the same as the methodfor manufacturing connection structure according to the fifth embodimentexcept that the second composite 30′ is arranged on the second electrode114 and a region other than the second electrode 114 of the secondsurface. The same description as that of the first embodiment and thefifth embodiment is omitted, and parts different from the method formanufacturing connection structure according to the first embodiment andthe fifth embodiment are described herein.

The Method for Manufacturing Connection Structure

The method for manufacturing connection structure according to oneembodiment of the present invention is described by using FIG. 15A toFIG. 15F. Since the existing first electronic component 101 and secondelectronic component 111 can be used in the present embodiment, theirdescription is omitted. In FIG. 15A to FIG. 15F, the method of formingthe connection structure 100 b is described in detail.

First, the first composite 20′ is arranged on the first surface of thefirst member 102, and the plurality of conductive particles 10 arearranged on the upper surface of the first electrode 110. The pluralityof conductive particles 10 and the first composite 20′ are mixed, andare arranged by using an offset printing scheme. Since the mixture ofthe conductive particles 10 and the first composite 20′ contains theconductive particles 10, a pad printing scheme of transferring a printedmatter by using a pad is particularly preferable. The region and methodfor arranging the mixture of the plurality of conductive particles 10and the first composite 20′ are the same as those of the method formanufacturing connection structure according to the fifth embodiment,and are therefore not described herein.

FIG. 15A and FIG. 15B show a process of transferring the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe pad 230 to the first surface of the first member 102. As shown inFIG. 15A and FIG. 15B, the pad 230 is pressed in a directionsubstantially perpendicular to the first surface, and is then pulledaway in the direction substantially perpendicular to the first surface,thereby transferring the mixture of the conductive particles 10 and thefirst composite 20′ displaced to the pad 230 onto the first surface.Here, the first composite 20′ and the conductive particles 10transferred from the depressed parts 246 of the plate 240 are arrangedso as to be in contact with the first electrode 110. That is, the firstcomposite 20 is arranged on the first surface of the first member 102,and the conductive particles 10 are arranged on the upper surface of thefirst electrode 110. The viscosity of the curable resin material of thefirst composite 20′ is in the range between a value equal to or higherthan 5×10³ cP and a value equal to or lower than 5×10⁵ cP. Thus, theconductive particles 10 mixed into the first composite 20′ can beretained on the first electrode 110. The use of this method allows theconductive particles 10 and the first composite 20′ to be reliablyarranged in a predetermined region on the first electrode 110.

With the depth of the depressed parts 246, the first composite 20′ andthe conductive particles 10 transferred from the depressed parts 246 ofthe plate 240 are thickly arranged in the opposing direction (D1direction) of the electrodes on the first electrode 110 on the firstmember 102. On the other hand, without the depth of the depressed parts246, the first composite 20′ transferred from the upper surface 244 ofthe plate 240 is thinly arranged in the opposing direction (D1direction) of the electrodes in the region other than the firstelectrode 110 on the first member 102. However, this is not meant to berestrictive, and the first composite 20′ may not be transferred from theupper surface 244 of the plate 240 to the pad 230. On the first surfaceof the first member 102, the first composite 20′ forms a convex/concaveconfiguration in the opposing direction (D1 direction) of theelectrodes. On the first surface of the first member 102, the conductiveparticles 10 form a convex configuration together with the firstcomposite 20′. In the present embodiment, the plate 240 is smaller thanthe first surface (connection surface) of the first member 102. Thus,the first composite 20′ is not arranged at the end of the first surface.

Next, the second composite 30′ is arranged on the second surface of thesecond member 112. As shown in FIG. 15C and FIG. 15D, the secondcomposite 30′ is arranged in a region other than the second electrode114 of the second surface of the second member 112. Furthermore, thesecond composite 30′ is arranged also on the second electrode 114 of thesecond surface. The second composite 30′ is arranged also at the end ofthe second surface. In the present embodiment, the second composite 30′is in a paste form, and is arranged by using an inkjet scheme or jetdispensing scheme. However, the method of arranging the second composite30′ is not limited to this scheme, and any existing method can be used.For example, coating by inkjet or a dispenser, screen printing, or thelike can be used.

The viscosity of the second composite 30 is in a range between a valueequal to or higher than 2×10³ cP and a value equal to or lower than2×10⁵ cP. This allows a flow of the second composite 30′ to beinhibited.

Next, the second member 112 is mounted on the first surface of the firstmember 102. As shown in FIG. 15E, the first surface of the first member102 and the second surface of the second member 112 are arranged so asto be opposed to each other so that the corresponding plurality of firstelectrodes 110 and the plurality of second electrodes 114 are opposed toeach other. The first member 102 and the second member 112 are pressedso that the first surface of the first member 102 and the second surfaceof the second member 112 are pushed in directions substantiallyperpendicular to the respective surfaces. The first surface of the firstmember 102 and the second surface of the second member 112 arepressure-welded to the conductive particles 10, the first composite 20′,and the second composite 30′. Here, the first composite 20′ arranged onthe first electrode 110 has a viscosity higher than that of the secondcomposite 30′, and is thus retained on the first electrode 110 togetherwith the conductive particles 10. The second composite 30′ arranged onthe second electrode 114 has a viscosity lower than that of the firstcomposite 20′, and thus mostly moves to a region other than the firstelectrode 110 where the conductive particles 10 and the first composite20′ are arranged. That is, with a stress being applied between the firstsurface of the first member 102 and the second surface of the secondmember 112, most of the second composite 30′ positioned between thesecond electrode 114 and the first composite 20′ moves and the secondcomposite 30′ positioned between the second electrode 114 and theconductive particles 10 is eliminated. Furthermore, the first composite20′ and the conductive particles 10 forming the convex/concaveconfiguration on the first surface of the first member 102 are buried bythe second composite 30′. In other words, most of the second composite30′ is arranged on the second surface of the second member 112 in aregion other than the region where the plurality of conductive particles10 and the first composite 20′ are arranged (convex configuration). Thesecond composite 30′ is arranged on the surface of the first member 102and a region where the first composite 20′ is arranged (concaveconfiguration). The conductive particles 10 arranged on the firstelectrode 110 are arranged so as to be in contact with the secondelectrode 114, and the second composite 30′ is arranged so as to be incontact with the first composite 20′ arranged in a region other than thefirst electrode 110 on the first surface, a region other than the secondelectrode 114 on the second surface, and the second electrode 114.

As shown in FIG. 15F, the first member 102 and the second member 112 arefurther pressed to push the first surface of the first member 102 andthe second surface of the second member 112 in the directionssubstantially perpendicular to the respective surfaces. Here, asufficient pressure is applied cause the opposing first electrode 110and second electrode 114 to be in contact with upper and lower sides ofone conductive particle 10. The pressure to push the first surface ofthe first member 102 and the second surface of the second member 112 canbe adjusted as appropriate by a repulsive force of the conductiveparticles 10 and elastic forces of the first composite 20′ and thesecond composite 30′. This configuration allows electrical connectionbetween the first electrode 110 and the second electrode 114.

With the first member 102 and the second member 112 pressed, theconnection structure 100 b is irradiated with light to cure the firstcomposite 20′ and the second composite 30′. A method of curing the firstcomposite 20′ and the second composite 30′ is the same as that of themethod for manufacturing connection structure according to the firstembodiment, and is therefore not described herein. By curing the firstcomposite 20 and the second composite 30′, the first resin 20 and thesecond resin 30 are formed. This configuration allows physicalconnection between the first surface of the first electronic component101 and the second surface of the second electronic component 111.

According to the present embodiment, a connection structure and a methodfor manufacturing connection structure can be provided that can ensureconductivity between the opposing electrodes with a simple process andcan reduce a short circuit between adjacent connection electrodes, evenif the electrodes arranged on the electronic component have highfineness and high density. Furthermore, since no heat curing connectionscheme is used, the electrodes of the upper and lower substrates havingdifferent coefficients of thermal expansion can be connected with highaccuracy.

Seventh Embodiment

The configuration of a connection structure according to a seventhembodiment is the same as the configuration of the connection structureaccording to the third embodiment except that the first resin 20 isarranged also in a region other than the second electrode of the secondmember 112. The configuration of the connection structure according tothe present embodiment is the same as the configuration of theconnection structure according to the fifth embodiment except thelamination order of the first resin 20 and the second resin 30 arrangedbetween the first surface and the second surface. A method formanufacturing connection structure according to the present embodimentis the same as the method for manufacturing connection structureaccording to the first embodiment and the fifth embodiment except thatthe first composite 20′ is arranged on the second electrode 114 and aregion other than the second electrode 114 of the second surface and thesecond composite 30′ is arranged on the second electrode 114 and aregion other than the second electrode 114 of the second surface. Thesame description as that of the first embodiment and the fifthembodiment is omitted, and parts different from the connectionstructures and the method for manufacturing connection structureaccording to the first embodiment and the fifth embodiment are describedherein.

Configuration of Connection Structure

FIG. 16A to FIG. 16C show the configuration of the connection structureaccording to one embodiment of the present invention. FIG. 16A is a planview of the connection structure according to one embodiment of thepresent invention. FIG. 16B is a sectional view along an I-I′ line ofFIG. 16A. FIG. 16C is an enlarged sectional view of a conductiveparticle region J of FIG. 16B.

As shown in FIG. 16A and FIG. 16B, a connection structure 100 c includesthe first member 102 having the first surface the first electrode 110,the second member 112 having the second surface, the second electrode114, the conductive particles 10, the first resin 20, and the secondresin 30. A plurality of first electrodes 110 and a plurality of secondelectrode 114 are arranged so as to be the first electrode 110 and thesecond electrode 114 are opposed to each other. The plurality ofconductive particles 10, the first resin 20, and the second resin 30 arearranged between the opposing first electrode 110 and second electrode114. The plurality of conductive panicles 10 are arranged in the surfacedirection (D2-D3 surface direction) between the opposing first electrode110 and second electrode 114. One conductive particle 10 is arrangedbetween the opposing first electrode 111 and second electrode 114 in theopposing direction (D1 direction) of the first electrode 110 and thesecond electrode 114. Each of the plurality of conductive particles 10are in contact with the opposing first electrode 110 and secondelectrode 114. As shown in FIG. 16C, the conductive particle 10 ispressured and deformed in the opposing direction (D1 direction) betweenthe first electrode 110 and the second electrode 114 by a method formanufacturing connection structure which will be described furtherbelow. That is, a distance between the first electrode 110 and thesecond electrode 114 in the opposing direction (D1 direction) of theelectrodes is substantially equal to the height of the conductiveparticle 10 in the opposing direction (D1 direction) of the electrodes.The height of the conductive particle 10 in the opposing direction (D1direction) of the electrodes is pressured and deformed by approximately10% to 40%. With a stress provided among the first electrode 110, theconductive particles 10, and the second electrode 114, the first resin20 and the second resin 30 are eliminated at the contact part betweenthe first electrode 110 and the conductive particle 10 and the contactpart between the second electrode 114 and the conductive particle 10.Furthermore, even if aural oxide film is formed on the first electrode110, the conductive particle 10, or the second electrode 114 and itssurface is insulated, the first electrode 110 and the second electrode114 are pressure-welded with the conductive particle 10 interposedtherebetween, thereby breaking the natural oxide film to form aconductive route. Furthermore, deformation of the conductive particle 10can increase the area of contact between the first electrode 110 and theconductive particle 10 and the area of contact between the secondelectrode 114 and the conductive particle 10. This arrangement allowsthe conductive particle 10 to electrically connect the first electrode110 and the second electrode 114.

In the present embodiment, the first resin 20 is arranged also in aregion other than the second electrode 114 of the second surface whenviewed in the opposing direction (D1 direction) of the electrodes. Thefirst resin 20 is arranged also between the plurality of secondelectrodes 114 and around the plurality of second electrodes 114 on thesecond surface when viewed in the opposing direction (D1 direction) ofthe electrodes. On the other hand, the first resin 20 is not arranged atan end of the second surface when viewed in the opposing direction (D1direction) of the electrodes. Here, the conductive particles 10 are notarranged in a region other than the first electrode 110 of the firstsurface (the second electrode 114 of the second surface) when viewed inthe opposing direction (D1 direction) of the electrodes. That is, theconductive particles 10 are arranged on the first electrode 110 (or thesecond electrode 114).

The second resin 30 is further arranged between the first surface of thefirst member 102 and the second surface of the second member 112. Thesecond resin 30 is arranged in a region not between the opposing firstelectrode 110 and second electrode 114. It the present embodiment, thesecond resin 30 is arranged in a region other than the first electrode110 of the first surface when viewed in the opposing direction (D1direction) of the electrodes. That is, the second resin 30 is arrangedon the first surface of the first member 102 between the plurality offirst electrodes 110 adjacent to each other in the surface direction(D2-D3 surface direction) and on the periphery thereof. The second resin30 is arranged also at ends of the first surface and the second surfacewhen viewed in the opposing direction (D1 direction) of the electrodes.As shown in FIG. 16B and FIG. 16C, the second resin 30 is furtherarranged also between the first electrode 110 and the second electrode114 in the region where the conductive particles 10 and the first resin20 are arranged. The second resin 30 is arranged between the first resin20 and the first electrode 110. That is, when viewed in the opposingdirection (D1 direction) of the electrodes, the conductive particles 10arranged on the first electrode 110 on the first surface of the member102 are surrounded by the second resin 30 in the surface direction(D2-D3 surface direction). The first resin 20 and the second resin 30are insulating resin. Thus, the connection structure 100 c hasinsulation properties in the surface direction (D2-D3 surfacedirection). This arrangement allows the second resin 30 to reliablyinsulate between the plurality of first electrodes 110 adjacent in thesurface direction (D2-D3 surface direction), between the plurality ofsecond electrodes 114 adjacent in the surface direction (D2-D3 surfacedirection), and between the first electrode 110 and the second electrode114 not opposed to each other.

The first resin 20 and the second resin 30 are arranged between theregion other than the first electrode 110 of the first surface and theregion other than the second electrode 114 of the second surface. Thefirst resin 20 and the second resin 30 are arranged between theplurality of first electrodes 110 adjacent to each other in the surfacedirection (D2-D3 surface direction) and on the periphery thereof andbetween the plurality of second electrodes 114 adjacent each other inthe surface direction (D2-D3 surface direction) and on the peripherythereof. Furthermore, the first resin 20 and the second resin 30 arearranged also between the first electrode 110 and the second electrode114. The first resin 20 is arranged so as to be in contact with thesecond surface, and the second resin 30 is arranged so as to be incontact with the first surface. That is, the first resin 20 and thesecond resin 30 are in contact in the surface direction (D2-D3 surfacedirection) between the first surface of the first electronic component101 and the second surface of the second electronic component 111 andare laminated in the opposing direction (D1 direction) of theelectrodes. On the other hand, the second resin 30 is arranged at theends of the first surface and the second surface when viewed in theopposing direction (D1 direction) of the electrodes.

The Method for Manufacturing Connection Structure

The method for manufacturing connection structure according to oneembodiment of the present invention is described by using FIG. 17A toFIG. 17E. Since the existing first electronic component 101 and secondelectronic component 111 can be used in the present embodiment, theirdescription is omitted. In FIG. 17A to FIG. 17E, the method of formingthe connection structure 100 c is described in detail.

First, the first composite 20′ is arranged on the second surface of thesecond member 112, and the plurality of conductive particles 10 arearranged on the upper surface of the second electrode 114. The pluralityof conductive particles 10 and the first composite 20′ are mixed, andare arranged by using an offset printing scheme. Since the mixture ofthe conductive particles 10 and the first composite 20′ contains theconductive particles 10, a pad printing scheme of transferring a printedmatter by using a pad is particularly preferable. The region and methodfor arranging the mixture of the plurality of conductive particles 10and the first composite 20′ are the same as those of the method formanufacturing connection structure according to the fifth embodiment,and are therefore not described herein.

FIG. 17A and FIG. 17B show a process of transferring the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe pad 230 to the second surface of the second member by the padprinting scheme. As shown in FIG. 17A and FIG. 17B, the pad 230 ispressed in a direction substantially perpendicular to the secondsurface, and is then pulled away in the direction substantiallyperpendicular to the second surface, thereby transferring the mixture ofthe conductive particles 10 and the first composite 20′ displaced to thepad 230 onto the second surface. Here, the first composite 20′ and theconductive particles 10 transferred from the depressed parts 246 of theplate 240 are arranged so as to be in contact with the second electrode114. That is, the first composite 20′ is arranged on the second surfaceof the second member 112, and the conductive particles 10 are arrangedon the upper surface of the second electrode 114. The viscosity of thecurable resin material of the first composite 20′ is in the rangebetween a value equal to or higher than 5×10³ cP and a value equal to orlower than 5×10⁵ cP. Thus, the conductive particles 10 mixed into thefirst composite 20′ can be retained on the second electrode 114. The useof this method allows the conductive particles 10 and the firstcomposite 20′ to be reliably arranged in a predetermined region on thesecond electrode 114.

With the depth of the depressed parts 246, the first composite 20′ andthe conductive particles 10 transferred from the depressed parts 246 ofthe plate 240 are thickly arranged in the opposing direction (D1direction) of the electrodes on the second electrode 114 on the secondmember 112. On the other hand, without the depth of the depressed parts246, the first composite 20′ transferred from the upper surface 244 ofthe plate 240 is thinly arranged in the opposing direction (D1direction) of the electrodes in the region other than the secondelectrode 114 on the second member 112. However, this is not meant to berestrictive, and the first composite 20′ may not be transferred from theupper surface 244 of the plate 240 to the pad 230. On the second surfaceof the second member 112, the first composite 20′ forms a convex/concaveconfiguration in the opposing direction (D1 direction) of theelectrodes. On the second surface of the second member 112, theconductive particles 10 form a convex configuration together with thefirst composite 20′. In the present embodiment, the plate 240 is smallerthan the second surface (connection surface) of the second member 112.Thus the first composite 20′ is not arranged at the end of the secondsurface.

Next, the second co composite 30′ is arranged on the second surface ofthe second member 112. As shown in FIG. 17C, the second composite 30′ isarranged in a region other than the second electrode 114 of the secondsurface of the second member 112. Furthermore, the second composite 30′is arranged also on the second electrode 114 of the second surface.Here, the first composite 20′ transferred from the upper surface 244 ofthe plate 240 is arranged in a region other than the second electrode114 of the second surface. Also the conductive particles 10 and thefirst composite 20′ transferred from the depressed parts 246 of theplate 240 are arranged on the second electrode 114 of the secondsurface. Thus, the second composite 30′ is arranged to be superposed soas to be in contact with the conductive particles 10 and the firstcomposite 20′. The second composite 30′ is arranged also at the end ofthe second surface. In the present embodiment, the second composite 30is in a paste form, and is ranged by using an inkjet scheme or jetdispensing scheme. However, the method of arranging the second composite30′ is not limited to this scheme, and any existing method can be used.For example coating by inkjet or a dispenser, screen printing, or thelike can be used.

The viscosity of the second composite 30′ is in a range between a valueequal to or higher than 2×10³ cP and a value equal to or lower than2×10⁵ cP. It is required that the viscosity of the first composite 20′is twice as high as high as the viscosity of the second composite 30′ orhigher. This allows a flow of the conductive particles 10 mixed into thefirst composite 20′ to be inhibited and the conductive particles 10 canbe retained on the first electronic component 110.

Next, the second electronic component 111 is mounted on surface of thefirst electronic component 101. As shown in FIG. 17D, the first surfaceof the first member 102 and the second surface of the second member 112are arranged so as to be opposed to each other so that the correspondingplurality of first electrodes 110 and the plurality of second electrodes114 are opposed to each other. The first member 102 and the secondmember 112 are pressed so that the first surface of the first member 102and the second surface of the second member 112 are pushed in directionssubstantially perpendicular to the respective surfaces. The firstsurface of the first member 102 and the second surface of the secondmember 112 are pressure-welded to the conductive particles 10, the firstcomposite 20′, and the second composite 30′. Here, the first composite20′ arranged on the second electrode 114 has a viscosity higher thanthat of the second composite 30′, and is thus retained on the secondelectrode 114 together with the conductive particles 10. The secondcomposite 30′ arranged on the second electrode 114 has a viscosity lowerthan that of the first composite 20′, and thus mostly moves to a regionother than the second electrode 114 where the conductive particles 10and the first composite 20′ are arranged. That is, with a stress beingapplied between the first surface of the first member 102 and the secondsurface of the second member 112, most of the second composite 30′positioned between the first electrode 110 and the first composite 20′moves, and the second composite 30′ positioned between the firstelectrode 110 and the conductive particles 10 is eliminated.Furthermore, the first composite 20′ and the conductive particles 10forming the convex/concave configuration on the second surface of thesecond member 112 are buried by the second composite 30′. In otherwords, most of the second composite 30′ is arranged on the first surfaceof the first member 102 in a region other than the region where theplurality of conductive particles 10 and the first composite 20′ arearranged (convex configuration). The second composite 30′ is arranged onthe first surface of the first member 102 and a region where the firstcomposite 20′ is arranged (concave configuration). The conductiveparticles 10 arranged on the second electrode 114 are arranged so as tobe in contact with the first electrode 110, and the second composite 30′is arranged so as to be in contact with the first composite 20′ arrangedin a region other than the second electrode 114 on the second surface, aregion other than the first electrode 110 on the first surface, and thefirst electrode 110.

As shown in FIG. 17E, the first member 102 and the second member 112 arefurther pressed to push the first surface of the first member 102 andthe second surface of the second member 112 in the directionssubstantially perpendicular to the respective surfaces. Here, asufficient pressure is applied to cause the opposing first electrode 110and second electrode 114 to be in contact with upper and lower sides ofone conductive particle 10. The pressure to push the first surface ofthe first member 102 and the second surface of the second member 112 canbe adjusted as appropriate by a repulsive force of the conductiveparticles 10 and elastic forces of the first composite 20′ and thesecond composite 30′. This configuration allows electrical connectionbetween the first electrode 110 and the second electrode 114.

With the first member 102 and the second member 112 pressed, theconnection structure 100 c is irradiated with light to cure the firstcomposite 20′ and the second composite 30′. A method of curing the firstcomposite 20′ and the second composite 30′ is the same as that of themethod for manufacturing connection structure according to the firstembodiment, and is therefore not described herein. By curing the firstcomposite 20′ and the second composite 30′, the first resin 20 and thesecond resin 30 are formed. This configuration allows physicalconnection between the first surface of the first electronic component101 and the second surface of the second electronic component 111.

According to the present embodiment, a connection structure and a methodfor manufacturing connection structure can be provided that can insureconductivity between the opposing electrodes with a simple process andcan reduce a short circuit between adjacent connection electrodes, evenif the electrodes arranged on the electronic component have highfineness and high density. Furthermore since no heat curing connectionscheme is used, the electrodes of the upper and lower substrates havingdifferent coefficients of thermal expansion can be connected with highaccuracy.

Eighth Embodiment

The configuration of a connection structure according to an eighthembodiment is the same as the configuration connection structureaccording to the seventh embodiment. A method for manufacturingconnection structure according to the present embodiment is the same asthe method for manufacturing connection structure according to theseventh embodiment except that the second composite 30′ is arranged onthe first electrode 110 and a region other than the first electrode 110of the first surface. The same description as that of the firstembodiment, the fifth embodiment, and the seventh embodiment is omitted,and parts different from the method for manufacturing connectionstructure according to the first embodiment, the fifth embodiment, andthe seventh embodiment are described herein.

The Method for Manufacturing Connection Structure

The method for manufacturing connection structure according to oneembodiment of the present invention is described by using FIG. 18A toFIG. 18F. Since the existing first electronic component 101 and secondelectronic component 111 can be used in the present embodiment, theirdescription is omitted. In FIG. 18A to FIG. 18F, the method of formingthe connection structure 100 c is described in detail.

First, the first composite 20′ is arranged on the second surface of thesecond member 112, and the plurality of conductive particles 10 arearranged on the upper surface of the second electrode 114. The pluralityof conductive particles 10 and the first composite 20′ are mixed, andare arranged by using an offset printing scheme. Since the mixture ofthe conductive particles 10 and the first composite 20′ contains theconductive particles 10, a pad printing scheme of transferring a printedmatter by using a pad is particularly preferable. The region and methodfor arranging the mixture of the plurality conductive particles 10 andthe first composite 20′ are the same as those of the method formanufacturing connection structure according to the fifth embodiment andare therefore not described herein.

FIG. 18A and FIG. 18B show a process of transferring the mixture of theplurality of conductive particles 10 and the first composite 20′ fromthe pad 230 to the second surface of the second member 112 by the padprinting scheme. As shown in FIG. 18A and FIG. 18B, the pad 230 ispressed in a direction substantially perpendicular to the secondsurface, and is then pulled away in the direction substantiallyperpendicular to the second surface, thereby transferring the mixture ofthe conductive particles 10 and the first composite 20′ displaced to thepad 230 onto the second surface. Here, the first composite 20′ and theconductive particles 10 transferred from the depressed parts 246 of theplate 240 are arranged so as to be in contact with the second electrode114. That is, the first composite 20′ is arranged on the second surfaceof the second member 112, and the conductive particles 10 are arrangedon the upper surface of the second electrode 114. The viscosity of thecurable resin material of the first composite 20′ is in the rangebetween a value equal to or higher than 5×10³ cP and a value equal to orlower than 5×10⁵ cP. Thus, the conductive particles 10 mixed into thefirst composite 20′ can be retained on the second electrode 114. The useof this method allows the conductive particles 10 and the firstcomposite 20′ to be reliably arranged in a predetermined region on thesecond electrode 114.

With the depth of the depressed parts 246, the first composite 20′ andthe conductive particles 10 transferred from the depressed parts 246 ofthe plate 240 are thickly arranged in the opposing direction (D1direction) of the electrodes on the second electrode 114 on the secondmember 112. On the other hand, without the depth of the depressed parts246, the first composite 20′ transferred from the upper surface 244 ofthe plate 240 is thinly arranged in the opposing direction (D1direction) of the electrodes in the region other than the secondelectrode 114 on the second member 112. However, this is not meant to berestrictive, and the first composite 20′ may not be transferred from theupper surface 244 of the plate 240 to the pad 230. On the second surfaceof the second member 112, the first composite 20′ forms a convex/concaveconfiguration in the opposing direction (D1 direction) of theelectrodes. On the second surface of the second member 112, theconductive particles 10 form a convex configuration together with thefirst composite 20′. In the present embodiment, the plate 240 is smallerthan the second surface (connection surface) of the second member 112.Thus, the first composite 20′ is not arranged at the end of the secondsurface.

Next, the second composite 30′ is arranged on the first surface of thefirst member 102. As shown in FIG. 18C and FIG. 18D, the secondcomposite 30′ is arranged in a region other than the first electrode 110of the first surface of the first member 102. Furthermore, the secondcomposite 30′ is arranged also on the first electrode 110 of the firstsurface. The second composite 30′ is arranged also at the end of thefirst surface. In the present embodiment, the second composite 30′ is ina paste form, and is arranged by using an inkjet scheme or jetdispensing scheme. However, the method of arranging the second composite30′ is not limited to this scheme, and any existing method can be used.For example, coating by inkjet or a dispenser, screen printing, or thelike can be used.

The viscosity of the second composite 30′ is in a range between a valueequal to or higher than 2×10³ cP and a value equal to or lower than2×10⁵ cP. This allows a flow of the second composite 30 to be inhibited.

Next, the second electronic component 111 is mounted on the firstsurface of the first electronic component 101. As shown in FIG. 18E, thefirst surface of the first member 102 and the second surface of thesecond member 112 are arranged so as to be opposed to each other so thatthe corresponding plurality of first electrodes 110 and the plurality ofsecond electrodes 114 are opposed to each other. The first member 102and the second member 112 are pressed so that the first surface of thefirst member 102 and the second surface of the second member 112 arepushed in directions substantially perpendicular to the respectivesurfaces. The first surface of the first member 102 and the secondsurface of the second member 112 are pressure-welded to the conductiveparticles 10, the first composite 20′, and the second composite 30′.Here, the first composite 20′ arranged on the second electrode 114 has aviscosity higher than that of the second composite 30′, and is thusretained on the second electrode 114 together with the conductiveparticles 10. The second composite 30′ arranged on the first electrode110 has a viscosity lower than that of the first composite 20′, and thusmostly moves to a region other than the second electrode 114 where theconductive particles 10 and the first composite 20′ are arranged. Thatis, with a stress being applied between the first surface of the firstmember 102 and the second surface of the second member 112, most of thesecond composite 30′ positioned between the first electrode 110 and thefirst composite 20′ moves, and the second composite 30′ positionedbetween the first electrode 110 and the conductive particles 10 iseliminated. Furthermore, the first composite 20′ and the conductiveparticles 10 forming the convex/concave configuration on the secondsurface of the second member 112 are buried by the second composite 30′.In other words, most of the second composite 30 is arranged on the firstsurface of the first member 102 in a region other than the region wherethe plurality of conductive particles 10 and the first composite 20′ arearranged (convex configuration). The second composite 30′ is arranged onthe first surface of the first member 102 and a region when the firstcomposite 20′ is arranged (concave configuration). The conductiveparticles 10 arranged on the second electrode 114 are arranged so as tobe in contact with the first electrode 110, and the second composite 30′is arranged so as to be in contact with the first composite 20′ arrangedin a region other than the second electrode 114 on the second surface, aregion other than the first electrode 110 on the first surface, and thefirst electrode 110.

As shown in FIG. 18F, the first member 102 and the second member 112 arefurther pressed to push the first surface of the first member 102 andthe second surface of the second member 112 in the directionssubstantially perpendicular to the respective surfaces. Here, sufficientpressure is applied to cause the opposing first electrode 110 and secondelectrode 114 to be in contact with upper and lower sides of oneconductive particle 10. The pressure to push the first surface of thefirst member 102 and the second surface of the second member 112 can beadjusted as appropriate by a repulsive force of the conductive particles10 and elastic forces of the first composite 20′ and the secondcomposite 30′. This configuration allows electrical connection betweenin the first electrode 110 and the second electrode 114.

With the first member 102 and the second member 112 pressed, theconnection structure 100 c is irradiated with light to e the firstcomposite 20′ and the second composite 30′. A method of curing the firstcomposite 20′ and the second composite 30′ is the same as that of themethod for manufacturing connection structure according to the firstembodiment, and is therefore not described herein. By curing the firstcomposite 20′ and the second composite 30′, the first resin 20 and thesecond resin 30 are formed. This configuration allows physicalconnection between the first surface of the first electronic component101 and the second surface of the second electronic component 111.

According to present embodiment, a connection structure and a method formanufacturing connection structure can be provided that can ensureconductivity between the opposing electrodes with a simple process andcan reduce a short circuit between adjacent connection electrodes, evenif the electrodes arranged on the electronic component have highfineness and high density. Furthermore, since no heat curing connectionscheme is used, the electrodes of the upper and lower substrates havingdifferent coefficients of thermal expansion can be connected with highaccuracy.

The present invention is not limited to the above-described embodiments,and can be modified as appropriate in a range not deviating from thegist of the invention. Also, the embodiments can be combined asappropriate.

First Example

FIG. 19A and FIG. 19B show an example of a connection structureaccording to one example of the present invention. FIG. 19A is a diagramof an arrangement pattern of the conductive particles 10 and the firstresin 20 of a connection structure according to a first example of thepresent invention. FIG. 19B is a diagram of an arrangement pattern ofthe first resin 20 and the second resin 30 of the connection structureaccording to the first example of the present invention. Parameters ofthe connection structure of the first example are as follows.

-   -   Width (short side) (A1) of the first electrode 110=9 μm    -   Distance (B1) between the first electrodes 110=6 μm    -   Pitch (A1+B1=C1) of the first electrode 110=15 μm    -   Length (long side) (D1) of the first electrode 110=105 μm    -   Area (A1×D1) of the first electrode 110=945 μm²    -   Number of conductive particles 10 arranged per the first        electrode 110=19

Second Example

FIG. 20A and FIG. 20B show an example of a connection structureaccording to one example of the present invention. FIG. 20A is a diagramof an arrangement pattern of the conductive particles 10 and the firstresin 20 of a connection structure according to a second example of thepresent invention. FIG. 20B is a diagram of an arrangement pattern ofthe first resin 20 and the second resin 30 of the connection structureaccording to the second example of the present invention. Parameters ofthe connection structure of the second example are as follows.

-   -   Width (short side) (A2) of the first electrode 110=9 μm    -   Distance (B2) between the first electrodes 112=6 μm    -   Pitch (A2+B2=C2) of the first electrode 110=15 μm    -   Length (long side) (D2) of the first electrode 110=10 μm    -   Area (A2×D2) of the first electrode 110=945 μm²    -   Number of conductive particles 10 arranged per the first        electrode 110=26

Third Example

FIG. 21A and FIG. 21B show an example of a connection structureaccording to one example of the present invention. FIG. 21A is a diagramof an arrangement pattern of the conductive particles 10 and the firstresin 20 of a connection structure according to a third example of thepresent invention. FIG. 21B is a diagram of an arrangement pattern ofthe first resin 20 and the second resin 30 of the connection structureaccording to the third example of the present invention. Parameters ofthe connection structure of the third example are as follows.

-   -   Width (short side) (A3) of the first electrode 110=9 μm    -   stance (B3) between the first electrodes 110=6 μm    -   Pitch (A3+B3=C3) of the first electrode 110=15 μm    -   Length (long side) (D3) of the first electrode 110=7 μm    -   Area (A3×D3) of the first electrode 110=702 μm²    -   Area of one region where the conductive particles 10 and the        first resin 20 are arranged=40 μm²    -   Total area of regions where the conductive particles 10 and the        first resin 20 are arranged per electrode=280 μm²    -   Number of regions where the conductive particles 10 and the        first resin 20 are arranged per electrode=7    -   Number of conductive particles 10 arranged per region where the        conductive particles 10 and the first resin 20 are arranged=2    -   Number of conductive particles 10 arranged per electrode=14

Fourth Example

FIG. 22A and FIG. 22B show an example of a connection structureaccording to one example of the present invention. FIG. 22A is a diagramof an arrangement pattern of the conductive particles 10 and the firstresin 20 of a connection structure according to a fourth example of thepresent invention. FIG. 22B is a diagram of an arrangement pattern ofthe first resin 20 and the second resin 30 of the connection structureaccording to the fourth example of the present invention. Parameters ofthe connection structure of the fourth example are as follows.

-   -   Width (short side) (A4) of the first electrode 110=12 μm    -   Distance (B4) between the first electrodes 110=9 μm    -   Pitch (A4+B4=C4) of the first electrode 110=21 μm    -   Length (long side) (D4) of the first electrode 110=105 μm    -   Area (A4×D4) of the first electrode 110=1260 μm²    -   Area of one region where the conductive particles 10 and the        first resin 20 are arranged=113 μm²    -   Total area of regions where the conductive particles 10 and the        first resin 2 are arranged per electrode=791 μm²    -   Number of regions where the conductive particles 10 and the        first resin 20 are arranged per electrode=7    -   Number of conductive particles 10 arranged per region where the        conductive particles 10 and the first resin 20 are arranged=7    -   Number of conductive particles 10 arranged per first electrode        110=49

Fifth Example

FIG. 23A and FIG. 23B show an example of a connection structureaccording to one example of the present invention. FIG. 23A is a diagramof an arrangement pattern of the conductive particles 10 and the firstresin 20 of a connection structure according to a fifth example of thepresent invention. FIG. 23B is a diagram of an arrangement pattern ofthe first resin 20 and the second resin 30 of the connection structureaccording to the fifth example of the present invention. Parameters ofthe connection structure of the fifth example are as follows.

-   -   Width (short side) (A5) of the first electrode 110=9 μm    -   Distance (B5) between the first electrodes 110=6 μm    -   Pitch (A5+B5=C5) of the first electrode 110=15 μm    -   Length (long side) (D4) of the first electrode 110=84 μm    -   Area (A5×D5) of the first electrode 110=758 μm²    -   Area of one region where the conductive particles 10 and the        first resin 20 are arranged=64 μm²    -   Total area of regions where the conductive particles 10 and the        first resin 20 are arranged per electrode=448 μm²    -   Number of regions where the conductive particles 10 and the        first resin 20 are arranged per electrode=7    -   Number of conductive particles 10 arranged per region where the        conductive particles 10 and the first resin 20 are arranged=3    -   Number of conductive particles 10 arranged per electrode=21

Sixth Example

FIG. 24A and FIG. 24B show an example of a connection structureaccording to one example of the present invention. FIG. 24A is a diagramof an arrangement pattern of the conductive particles 10 and the firstresin 20 of a connection structure according to a sixth example of thepresent invention. FIG. 24B is a diagram of an arrangement pattern ofthe first resin 20 and the second resin 30 of the connection structureaccording to the sixth example of the present invention. Parameters ofthe connection structure of the sixth example are as follows.

-   -   Width (short side) (A6) of the first electrode 110=21 μm    -   Distance (B6) between the first electrodes 110=10 μm    -   Pitch (A6+B6=C6) of the first electrode 110=31 μm    -   Length (long side) (D6) of the first electrode 110=21 μm    -   Area (A6×D6) of the first electrode 110=441 μm    -   Area of the region α where the conductive particles 10 and the        first resin 20 are arranged=64 μm²    -   Total area of regions α where the conductive particles 10 and        the first resin 20 are arranged per electrode=128 μm²    -   Number of regions α where the conductive particles 10 and the        first resin 20 are arranged=2    -   Number of conductive particles 10 arranged per region α=3    -   Area of the region β where the conductive particles 10 and the        first resin 20 are arranged=40 μm²    -   Total area of regions β where the conductive particles 10 and        the first resin 20 are arranged per electrode=80 μm²    -   Number of regions β where the conductive particles 10 and the        first resin 20 are arranged=2    -   Number of conductive particles 10 arranged per region β=2    -   Number of conductive particles 10 arranged per electrode=10

Seventh Example

FIG. 25A and FIG. 25B show an example of a connection structureaccording to one example of the present invention. FIG. 25A is a diagramof an arrangement pattern of the conductive particles 10 and the firstresin 20 of a connection structure according to a seventh example of thepresent invention. FIG. 25B is a diagram of an arrangement pattern ofthe first resin 20 and the second resin 30 of the connection structureaccording to the seventh example of the present invention. Parameters ofthe connection structure of the seventh example are as follows.

-   -   Width (short side) (A7) of the first electrode 110=15 μm    -   Distance (B7) between the first electrodes 110=10 μm    -   Pitch (A7+B7=C7) of the first electrode 110=25 μm    -   Length (long side) (D7) of the first electrode 110=30 μm    -   Area (A7×D7) of the first electrode 110=450 μm².    -   Area of one region where the conductive particles 10 and the        first resin 20 are arranged=113 μm²    -   Total area of regions where the conductive particles 10 and the        first resin 20 are arranged per electrode 226=226 μm²    -   Number of regions where the conductive particles 10 and the        first resin 20 are arranged per electrode=2    -   Number of conductive particles 10 arranged per region where the        conductive particles 10 and the first resin 20 are arranged=7    -   Number of conductive particles 10 arranged per electrode=14

As shown in the first to seventh examples, according to one embodimentof the present invention, even if the electrodes arranged on theelectronic components have high fineness and high density, conductivitybetween opposing electrodes is ensured with simple process, and a shortcircuit between adjacent electrodes can be reduced.

What is claimed is:
 1. A method for manufacturing connection structure,the method comprising: arranging a first composite and conductiveparticles in a recessed portion of a first planographic intaglio plate;displacing the first composite and the conductive particles from thefirst planographic intaglio plate to a pad; transferring the conductiveparticles and the first composite on a plurality of first electrodeslocated on a first surface of a first member from the pad, so that theconductive particles are arranged only on the plurality of firstelectrodes, each of the conductive particles comprises a particle corehaving elasticity coated with metals; arranging a second composite onthe plurality of first electrodes and a first region between theadjacent first electrodes of the first surface by a pad printing schemeusing a second planographic intaglio plate, so that the second compositeon the plurality of first electrodes is more thinly arranged than thesecond composite on the first region; arranging the first surface and asecond surface of a second member where a plurality of second electrodesis located, so that the plurality of first electrodes and the pluralityof second electrodes are opposed to each other; pressing the firstmember and the second member; and curing the first composite and thesecond composite.
 2. The method according to claim 1, wherein the secondcomposite is arranged on the plurality of second electrodes and a secondregion between the adjacent second electrodes of the second surfaceinstead of arranging on the first surface by a pad printing scheme usinga second planographic intaglio plate, so that the second composite onthe plurality of second electrodes is more thinly arranged than thesecond composite on the second region.
 3. The method according to claim1, wherein the first composite is further arranged on an upper surfaceof the first planographic intaglio plate when the first composite andthe conductive particles are arranged in the recessed portion of thefirst planographic intaglio plate; wherein the first composite isfurther transferred on a first region between the adjacent firstelectrodes of the first surface from the pad, when the conductiveparticles and the first composite are transferred on the plurality offirst electrodes.
 4. The method according to claim 3, wherein the firstcomposite is transferred on the plurality of first electrodes and thefirst region, so that the first composite on the plurality of firstelectrodes is more thickly arranged than the first composite on thefirst region.
 5. The method according to claim 1, wherein the firstcomposite has a viscosity higher than a viscosity of the secondcomposite.
 6. The method according to claim 1, wherein the conductiveparticles are mixed in the first composite in a range between a valueequal to or larger than 20 volume % and a value equal to or smaller than60 volume %.
 7. The method according to claim 1, wherein the firstcomposite and the second composite contain a radical-polymerizationresin.
 8. The method according to claim 1, wherein the second compositecontains an ene/thiol-based curable resin containing an ethyleneunsaturated compound and a thiol compound, and a curable component of atleast one of the ethylene unsaturated compound and the thiol compound isa 9,9-bisarylfluorene compound.
 9. The method according to claim 1,wherein the first composite and the second composite contain aphotocuring initiating component.
 10. The method according to claim 1,wherein the first composite and the second composite are cured by lightirradiation.
 11. The method according to claim 1, wherein the firstcomposite and the second composite contain a shielding part curingactivation compound.
 12. The method according to claim 1, wherein thefirst composite contains an anaerobic curing initiating component. 13.The method according to claim 1, wherein the first composite and thesecond composite are cured under the pressure.
 14. The method accordingto claim 1, wherein the conductive particle are in contact with at leastone of the plurality of first electrodes and at least one of theplurality of second electrodes by pressing the first member and thesecond member.
 15. A connection structure comprising: a first memberhaving a first surface; a plurality of first electrodes located on thefirst surface; a second member having a second surface opposed to thefirst surface; a plurality of second electrodes opposed to the pluralityof first electrodes and located on the second surface; a first resin andconductive particles arranged between at least one of the plurality offirst electrodes and at least one of the plurality of second electrodes,the conductive particles are arranged only on the plurality of firstelectrodes, each of the conductive particles comprises a particle corehaving elasticity coated with metals; and a second resin arrangedbetween the first surface and the second surface, the second resin on afirst region between the adjacent first electrodes is more thicklyarranged than the second resin on the plurality of first electrodes,wherein the first resin being in contact with the plurality of firstelectrodes, the second resin being in contact with the plurality ofsecond electrodes, and the first resin and the second resin beingdifferent compositions from each other.
 16. The connection structureaccording to claim 15, wherein the first resin is further arranged onthe first region, the first resin on the first region is more thinlyarranged than the first resin on the plurality of first electrodes, thefirst resin is in contact with the region other than the plurality offirst electrodes, and the second resin is in contact with the regionother than the plurality of second electrodes.
 17. The method accordingto claim 1, wherein the first composite is arranged only in the recessedportion of the first planographic intaglio plate; wherein the firstcomposite is transferred only on the plurality of first electrodes.